AA5052铝合金/AZ31B镁合金搅拌摩擦焊接头的腐蚀行为研究

doi:10.11896/cldb.21040318

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (27550KB)
Export: BibTeX | EndNote (RIS)

Abstract In this work, the friction stir welding was used to weld the Al/Mg alloy joints with good appearance. In order to study the corrosion behavior and corrosion mechanism, based on the analysis of the microstructure of the welded joint, the corrosion behavior of the welded joint was monitored and analyzed by the neutral salt spray corrosion test and electrochemical test, and the corrosion weight loss of the welded joint was analyzed. The results show that the inhomogeneity of the distribution of Al-Mg intermetallic compound and β phase in magnesium alloy in the stir zone and the thermo-mechanically affected zone, as well as the difference in the grain size of the region, leads to the difference in the tendency of forming primary batteries in the micro-plot of stirring zone and thermo-mechanically affected zone, thus showing the difference in corrosion morphology and corrosion behavior. The occurrence of galvanic corrosion leads to high corrosion current density in the welded joint, and the corrosion resistance is inferior to the base metal. During the whole neutral salt spray corrosion process, the mass loss is gradually increased, and the corrosion rate shows a downward trend after the first rise.

Key words： aluminum alloy magnesium alloy friction stir welding dissimilar joint corrosion behavior

Published: 25 February 2023 Online: 2023-03-02

CLC number:

TG172.2

Fund:Special Projects for the Central Government to Guide the Development of Local Science and Technology (2019ZYYD015).

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	CAI Da
	WANG Lishi
	HU Xinbin

Cite this article:

CAI Da,WANG Lishi,HU Xinbin. Study on Corrosion Behavior of Friction Stir Welded Joints of AA5052 Aluminum/AZ31B Magnesium Alloys[J]. Materials Reports, 2023, 37(4): 21040318-7.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.21040318 OR http://www.mater-rep.com/EN/Y2023/V37/I4/21040318

1 Chen Y H, Ni Q, Ke L M. Transactions of Nonferrous Metals Society of China, 2012, 22(2), 299.
2 Manladan S M, Yusof F, Ramesh S, et al. The International Journal of Advanced Manufacturing Technology, 2016, 90(1-4), 605.
3 Jing S, Kehong W, Qi Z, et al. Rare Metal Materials and Engineering, 2013, 42(7), 1337.
4 Sato Y, Shiota A, Kokawa H, et al. Science and Technology of Welding and Joining, 2010, 15(4), 319.
5 McLean A A, Powell G L, Brown I H, et al. Science and Technology of Welding and Joining, 2003, 8(6), 462.
6 Morishige T, Kawaguchi A, Tsujikawa M, et al. Materials Transactions, 2008, 49(5), 1129.
7 Lee W B, Yeon Y M, Jung S B. Journal of Materials Science, 2003, 38(20), 4183.
8 Ma Y W, Li Y B, Hu W, et al. Journal of Manufacturing Science and Engineering, 2016, 138(6), 061007.
9 Li Y, Wei Z, Wang Z, et al. Journal of Manufacturing Science and Engineering, 2013, 135(6), 061007.
10 Prabhuraj P, Rajakumar S, Balasubramanian V. Materials Today: Proceedings, 2020, 22, 546.
11 Li N, Che B, Wang Y S, et al. Hot Working Technology, 2018, 47(17), 201 (in Chinese).
李娜, 陈斌, 王艳松, 等. 热加工工艺, 2018, 47(17), 201.
12 Zhang M, Shen C B. Journal of Dalian Jiaotong University, 2019, 40(4), 82 (in Chinese).
张木, 沈长斌. 大连交通大学学报, 2019, 40(4), 82.
13 Savguira Y, North T H, Thorpe S J. Journal of The Electrochemical Society, 2018, 165(2), C1.
14 Zhang C H, Cao Y, Cao L F, et al. The Chinese Journal of Nonferrous Metals, 2019, 29(10), 2255 (in Chinese).
张成行, 曹宇, 曹玲飞, 等. 中国有色金属学报, 2019, 29(10), 2255.
15 Zheng B. Microstructure and properties for weld of friction stir welding for AZ31B Mg/5052Al dissimilar materials. Master's Thesis, Hubei University of Technology, China, 2020 (in Chinese).
郑博. AZ31B镁合金/5052铝合金异种材料搅拌摩擦焊组织与性能研究. 硕士学位论文, 湖北工业大学, 2020.
16 Meng Q, Liu Y, Kang J, et al. Transactions of Nonferrous Metals Society of China, 2019, 29(4), 701.
17 Masoudian A, Tahaei A, Shakiba A, et al. Transactions of Nonferrous Metals Society of China, 2014, 24(5), 1317.
18 Chen Y H, Xie J L, Ge J W, et al. Journal of Netshape Forming Engineering, 2015 , 7(5), 25 (in Chinese).
陈玉华, 谢吉林, 戈军委, 等. 精密成形工程, 2015, 7(5), 25.
19 Dong H R, Ma Y, Li W R. Materials for Mechanical Engineering, 2016, 40(10), 70 (in Chinese).
董海荣, 马颖, 李伟荣. 机械工程材料, 2016, 40(10), 70.
20 Zhang Z Y, Wang S L, Zhang H Y, et al. Journal of Chinese Society for Corrosion and Protection, 2017, 37(2), 117 (in Chinese).
张子阳, 王善林, 章恒瑜, 等. 中国腐蚀与防护学报, 2017, 37(2), 117.
21 Liu Y X. Rare Metal Materials and Engineering, 2021, 50(1), 361 (in Chinese).
刘玉项. 稀有金属材料与工程, 2021, 50(1), 361.
22 Wang X H, Wang JH, Fu C W. Transactions of Nonferrous Metals Society of China, 2014, 24(12), 3907.
23 Gupta R K, Das H, Pal T K. Journal of Materials Engineering and Performance, 2011, 21(8), 1645.
24 Jayaraj R K, Malarvizhi S, Balasubramanian V. Transactions of Nonferrous Metals Society of China, 2017, 27(10), 2181.
25 Kim S H, Erb U, Aust K T, et al. Scripta Materialia, 2001, 44( 5), 835.
26 Dan S, Ma A B, Jiang J, et al. Corrosion Science, 2010, 52(2), 481.
27 Tang C H, Cheng F T, Man H C. Materials Science & Engineering A, 2004, 373(1), 195.