| METALS AND METAL MATRIX COMPOSITES |
|
|
|
|
|
| Finite Element Analysis of Stress Field of C/C Composite Brazed Joint |
| LI Shengnan1,2,3, LU Quanbin3, DU Dong1, SUN Huawei4, ZHOU Xusheng3, LONG Weimin1,3,4,*
|
1 Department of Mechanical Engineering, Tsinghua University, Beijing 100084, China
2 State Key Laboratory for Performance and Structure Safety of Petroleum Tubular Goods and Equipment Materials, CNPC Tubular Goods Research Institute, Xi’an 710077, China
3 State Key Laboratory of Advanced Brazing Filler Metals & Technology, Zhengzhou Research Institute of Mechanical Engineering Co., Ltd., Zhengzhou 450001, China
4 China Academy of Machinery Ningbo Academy of Intelligent Machine Tool Co., Ltd., Ningbo 315700, Zhejiang, China |
|
|
|
|
Abstract Residual stress in brazed joint of dissimilar materials is one of the main reasons which result in low joint quality. The magnitude and distribution of residual stress in brazed joints of C/C composite and C/C composite, C/C composite and TiAl alloy were studied by numerical simulation method based on thermal-elastic-plastic theory and finite element software Abaqus as a platform. Furthermore, the influence of stress distribution on joint performance was revealed. Different Von Mises stress distribution and state appeared in different brazed joints. In C/C-C/C brazed joint, Von Mises stress was concentrated at the brazing seam, the edges and corners of C/C composite’s brazed surface, and gradually decreased from the outside to the inside. In C/C-TiAl brazed joint, the stress was concentrated on C/C composite where adjacent the brazing seam, and gradually decreased from inside to outside. The joint strength of brazed joint was mainly affected by the axial normal stress and the shear stress perpendicular to the axial direction. The residua stress of C/C-C/C brazed joint was lower, its axial tensile stress was almost zero, therefore the join strength of brazed joint was mainly affected by the shear stress. The residual stress of C/C-TiAl brazed joint was much higher, in C/C composite the maximum axial tensile stress was distributed at the edges, and the maximum shear stress was distributed inside of the brazed surface.
|
|
Published: 10 January 2023
Online: 2023-01-31
|
|
|
| Fund:National Natural Science Foundation of China (U2004186), and the Science and Technology Innovation ‘2025’ Major Project of Ningbo City (2020Z111). |
|
|
1 Albano M, Delfini A, Pastore R, et al. Acta Astronautica, 2016, 128, 277.
2 Devi G R, Rao K R. Defence Science Journal, 1993, 43(4), 369.
3 Yamaguchi M, Inui H, Ito K. Acta Materialia, 2000, 48(1), 307.
4 Li S N, Du D, Zhang L, et al. Materials, 2021, 14(8), 1844.
5 Li S N, Lu Q B, Du D, et al. Welding in the World. 2022, 66(1), 61.
6 Yi R X, Chen C, Shi C, et al. Ceramics International, 2021, 47, 20807.
7 Zhang X Y, Zhang F Q, Xia L H, et al. The Chinese Journal of Nonferrous Metals, 2012, 22(5), 1298(in Chinese).
张小英, 张福勤, 夏莉红, 等. 中国有色金属学报, 2012, 22(5), 1298.
8 Wang Y L, Wang W L, Huang J H, et al. Journal of Materials Processing Technology, 2021, 288, 116886.
9 Qin Y Q. Study on microstructure and mechanical properties of C/C composite and TC4 brazed joint. Ph. D. Thesis, Harbin Institute of Technology, China, 2007(in Chinese).
秦优琼. C/C复合材料与TC4钎焊接头组织及性能研究. 博士学位论文, 哈尔滨工业大学, 2007.
10 Ba J, Wang Y H, Liu Y L, et al. Vacuum, 2017, 143, 303.
11 Yang Z W, Wang C L, Han Y, et al. Carbon, 2019, 43, 494.
12 Guo W, Li K, Zhang H Q, et al. Ceramics International, 2022, 48(4), 5260.
13 Ba J, Ji X, Wang B, et al. Journal of Materials Science and Technology, 2022, 104, 33.
14 Ba J, Wang B, Ji X, et al. Ceramics International, 2020, 46, 14232.
15 Qi J L, Ba J, Li H, et al. Vacuum, 2020, 172, 109102.
16 Ba J, Ji X, Wang B, et al. Journal of Manufacturing Process, 2021, 67, 52.
17 Li S N, Du D, Zhang L, et al. Reviews on Advanced Materials Science, 2021, 60, 92.
18 Wang G, Jiao G Q, Li J. Mechanical Science and Technology for Aerospace Engineering, 2013, 32(12), 1807(in Chinese).
王刚, 矫桂琼, 李俊. 机械科学与技术, 2013, 32(12), 1807.
19 Deng J Y, Liu W C, Du H F. Chinese Journal of Materials Research, 2001, 15(3), 372(in Chinese).
邓景屹, 刘文川, 杜海峰. 材料研究学报, 2001, 15(3), 372.
20 Jiang W C, Gong J M, Chen H, et al. Acta Metallurgica Sinica, 2008, 44(1), 105(in Chinese).
蒋文春, 巩建鸣, 陈虎, 等. 金属学报, 2008, 44(1), 105.
21 Liu W S, Huang B Y, Zhou K Z, et al. Materials Reports, 2000, 14(9), 19(in Chinese).
刘文胜, 黄伯云, 周科朝, 等. 材料导报, 2000, 14(9), 19.
22 Sung S Y, Kim Y J. Intermetallics, 2007, 15, 468.
23 Hu H T, Zhang X W, Zhu C L, et al. Chinese Journal of Rare Metals, 2017, 41(7), 751(in Chinese).
胡海涛, 张熹文, 朱春雷, 等. 稀有金属, 2017, 41(7), 751. |
|
|
|
渝公网安备50019002502923号 © Editorial Office of Materials Reports.
2023, Vol. 37 