Abstract As one of the simple and convenient methods in preparing coatings, drying of colloidal suspension is widely used in protective and functional coatings. If not properly controlled, however, colloidal coatings are prone to cracking during the drying process, leading to the failure of coatings. Therefore, the mechanism of drying-induced cracking, as well as the methods to reduce cracking have been the focus of recent studies in both industrial and academic research of colloidal coatings.
Although empirical solutions for the crack suppression have been accumulated after many years of practice in preparing colloidal coating, the deep understanding of the drying-induced cracking is still lacking due to the complex film formation process in colloidal coatings. Conventional methods such as adding chemical binders in colloidal coatings to prevent cracking become unfeasiblefor coatings that need to meet higher environmental regulations and for the preparation of functional nanoparticle coatings. Therefore, extensive theoretical and experimental studies on the fundamental mechanism of drying-induced cracking have been carried out in academia and industry in recent years. Based on those findings, novel techniques for reducing and controlling crackings in drying colloidal coatings have been developed.
Theoretical models on the driving force and dynamics of drying-induced cracking have been proposed, aiming to reveal the mechanism of cracking from the perspectivesof the interaction between colloidal particles and the equilibrium between strain energy and surface energy. Many processing factors affecting the crack formation, including the colloidal particle network structure, thickness of coatings, the moduli of colloidal particles and the properties of substrates, were studied in order to understand how they affect the crack formation. Novel processing methods, including adding non-spherical particles, mixing of soft and hard particles, and multi-layer deposition, are proposed to suppress drying-induced cracking and improve the performance of coatings. On the other hand, recent studies proposed the utilization of coatings with cracks as the template to fabricate the micro-structure and nano-structure of metals and micro-channels and nano-channels by accurately controlling the morphology of drying-induced cracks of colloidal coatings.
This article reviewed recent studies on cracking in drying colloidal coatings. First, different crack morphologies are introduced and the mechanism and dynamics of cracking are discussed. Four main factors affecting the cracking of colloidal coatings and the corresponding methods for crack reduction are symmetrically summarized. In addition, the utilization of cracking in colloidal coating for alternative micro-fabrication and nano-fabrication is also explored. Further research on the cracking mechanism of colloidal particle coatings can provide design principles for the development of environment-friendly coatings and the design of high-quality functional nanoparticle coatings.

Key words： colloidal particle coating cracks in drying suppress the cracks applications of cracks

Published: 10 November 2022 Online: 2022-11-03

CLC number:	O648.14
	O345

Fund:National Natural Science Foundation of China (11674019, 12072010).

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	NIU Zhaoxia
	YUAN Shuaijie
	GAO Han
	XU Ye

Cite this article:

NIU Zhaoxia,YUAN Shuaijie,GAO Han, et al. Cracking in Drying Colloidal Coatings: Mechanism, Suppression and Applications[J]. Materials Reports, 2022, 36(21): 21050001-9.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.21050001 OR http://www.mater-rep.com/EN/Y2022/V36/I21/21050001

1 Ise N, Sogami I. Structure Formation in Solution: Ionic Polymers and Colloidal Particles. Springer Science & Business Media, Germany, 2005, pp. 119.
2 Saunders A E, Shah P S, Sigman M B, et al. Nano Letters, 2004,4, 1943.
3 Russel W B. AIChE Journal, 2011,57, 1378.
4 Martinez C J, Lewis J A. Journal of the American Ceramic Society, 2002,85, 2409.
5 Amalvy J I, Percy M J, Armes S P, et al. Langmuir, 2001,17, 4770.
6 Ge D T, Yang X M, Chen Z, et al. Nanoscale, 2017,9, 17357.
7 Wu G X, Zhao Y P, Ge D T, et al. Advanced Materials Interfaces, 2021,8, 2000681.
8 Roberts C C, Francis L F. Journal of Coatings Technology and Research, 2013,10, 441.
9 Pauchard L, Abou B, Sekimoto K. Langmuir, 2009,25, 6672.
10 Trueman R E, Lago Domingues E, Emmett S N, et al. Journal of Colloid and Interface Science, 2012,377, 207.
11 Zhou J J, Man X K, Jiang Y, et al. Advanced Materials, 2017,29, 1703769.
12 Dufresne E R, Corwin E I, Greenblatt N A, et al. Physical Review Letters, 2003,91, 224501.
13 Holmes D M, Kumar R V, Clegg W J. Journal of the American Ceramic Society, 2006,89, 1908.
14 Kiatkirakajorn P C, Goehring L. Physical Review Letters, 2015,115, 088302.
15 Hull D, Caddock B D. Journal of Materials Science, 1999,34, 5707.
16 Niu Z X, Huang T, Chen Y. Frontiers of Physics, 2018,13, 137804.
17 Huang J, Juszkiewicz M, de Jeu W H, et al. Science, 2007,317, 650.
18 Tirumkudulu M S, Russel WB. Langmuir, 2005,21, 4938.
19 Singh K B, Tirumkudulu M S. Physical Review Letters, 2007,98, 218302.
20 Qiao J, Adams J, Johannsmann D. Langmuir, 2012,28, 8674.
21 Bacchin P, Brutin D, Davaille A, et al. The European Physical Journal E, 2018,41, 94.
22 Kakui T, Miyauchi T, Kamiya H. Journal of the European Ceramic Society, 2005,25, 655.
23 McDonald B C, de Gouw J A, Gilman J B, et al. Science, 2018,359, 760.
24 McLachlan M A, Johnson N P, De La Rue R M, et al. Journal of Mate-rials Chemistry, 2004,14, 144.
25 Lazarus V, Pauchard L. Soft Matter, 2011,7, 2552.
26 Pauchard L, Adda-Bedia M, Allain C, et al. Physical Review E, 2003,67, 027103.
27 Han W, Li B, Lin Z. ACS Nano, 2013,7, 6079.
28 Sendova M, Willis K. Applied Physics A, 2003,76, 957.
29 Jin Q, Tan P, Schofield A B, et al. The European Physical Journal E, 2013,36, 28.
30 Goehring L, Clegg W J, Routh A F. Soft Matter, 2011,7, 7984.
31 Mondal I, Kumar A, Rao K D M, et al. Journal of Physics and Chemistry of Solids, 2018,118, 232.
32 Jing G Y, Ma J. The Journal of Physical Chemistry B, 2012,116, 6225.
33 Muzzillo C P, Reese M O, Mansfield L M. Langmuir, 2020,36, 4630.
34 Zhang Y J. Tuning of self-assembly patterns induced by the evaporation of colloidal droplets. Ph. D. Thesis, Northwestern Polytechnical University, China, 2015 (in Chinese).
张永健. 胶体液滴的蒸发及其自组装图案调控机制研究. 博士学位论文. 西北工业大学, 2015.
35 Goehring L, Morris S W. Journal of Geophysical Research: Solid Earth, 2008,113, B10203.
36 Goehring L, Clegg W J, Routh A F. Langmuir, 2010,26, 9269.
37 Li B, Jiang B, Han W, et al. Angewandte Chemie International Edition, 2017,56, 4554.
38 Kiruthika S, Rao K D M, Kumar A, et al. Materials Research Express, 2014,1, 026301.
39 Chen R, Zhang L, Zang D, et al. Advances in Colloid and Interface Science, 2016,231, 1.
40 Annarelli C C, Fornazero J, Bert J, et al. The European Physical Journal E, 2001,5, 599.
41 Xu Y, German G K, Mertz A F, et al. Soft Matter, 2013,9, 3735.
42 Gauthier G, Lazarus V, Pauchard L. EPL (Europhysics Letters), 2010,89, 26002.
43 Zarzycki J. Journal of Non-Crystalline Solids, 1988,100, 359.
44 Griffith A A, Taylor G I. Philosophical Transactions of the Royal Society of London Series A, Containing Papers of a Mathematical or Physical Cha-racter, 1921,221, 163.
45 Birk-Braun N, Yunus K, Rees E J, et al. Physical Review E, 2017,95, 022610.
46 Dufresne E R, Stark D J, Greenblatt N A, et al. Langmuir, 2006,22, 7144.
47 Goehring L, Clegg W J, Routh A F. Physical Review Letters, 2013,110, 024301.
48 Zarzycki J, Prassas M, Phalippou J. Journal of Materials Science, 1982,17, 3371.
49 Routh A F. Reports on Progress in Physics, 2013,76, 046603.
50 White L R. Journal of Colloid and Interface Science, 1982,90, 536.
51 Russel W B, Wu N, Man W. Langmuir, 2008,24, 1721.
52 Allain C, Limat L. Physical Review Letters, 1995,74, 2981.
53 Schneider M, Maurath J, Fischer S B, et al. ACS Applied Materials & Interfaces, 2017,9, 11095.
54 Kanai T, Sawada T. Langmuir, 2009,25, 13315.
55 Sibrant A L R, Pauchard L. EPL (Europhysics Letters), 2016,116, 49002.
56 Singh K B, Bhosale L R, Tirumkudulu M S. Langmuir, 2009,25, 4284.
57 Pauchard L, Parisse F, Allain C. Physical Review E, 1999,59, 3737.
58 Chiu R C, Garino T J, Cima M J. Journal of the American Ceramic Society, 1993,76, 2257.
59 Chiu R C, Cima M J. Journal of the American Ceramic Society, 1993,76, 2769.
60 Yow H N, Goikoetxea M, Goehring L, et al. Journal of Colloid and Interface Science, 2010,352, 542.
61 van der Kooij H M, van de Kerkhof G T, Sprakel J. Soft Matter, 2016,12, 2858.
62 Sommer A P, Franke R P. Nano Letters, 2003,3, 573.
63 Lama H, Basavaraj M G, Satapathy D K. Soft Matter, 2017,13, 5445.
64 Ghosh U U, Chakraborty M, Bhandari A B, et al. Langmuir, 2015,31, 6001.
65 Lei H, Payne J A, McCormick A V, et al. Journal of Applied Polymer Science, 2001,81, 1000.
66 Spry A. Journal of the Geological Society of Australia, 1962,8, 191.
67 Smith M I, Sharp J S. Langmuir, 2011,27, 8009.
68 Carreras E S, Chabert F, Dunstan D E, et al. Journal of Colloid and Interface Science, 2007,313, 160.
69 Koga S, Inasawa S. Colloids and Surfaces A: Physicochemical and Engineering Aspects, 2019,563, 95.
70 Lee W P, Routh A F. Industrial & Engineering Chemistry Research, 2006,45, 6996.
71 Keddie J, Routh A F. Fundamentals of Latex Film Formation: Processes and Properties. Springer Science & Business Media, 2010.
72 Hodges C S, Ding Y, Biggs S. Journal of Colloid and Interface Science, 2010,352, 99.
73 Qin F, Li M, Li X Y, et al. Applied Mechanics and Materials, 2015,731, 483.
74 Singh K B, Deoghare G, Tirumkudulu M S. Langmuir, 2009,25, 751.
75 Tzitzinou A, Keddie J L, Geurts J M, et al. Macromolecules, 2000,33, 2695.
76 Hasanzadeh I, Mahdavian A R, Salehi-Mobarakeh H. Progress in Organic Coatings, 2014,77, 1874.
77 Khan A K, Ray B C, Maiti J, et al. Pigment & Resin Technology, 2009,38, 159.
78 Geurts J, Bouman J, Overbeek A. Journal of Coatings Technology and Research, 2008,5, 57.
79 Limousin E, Ballard N, Asua J M. Journal of Applied Polymer Science, 2019,136, 47608.
80 Prosser J H, Brugarolas T, Lee S, et al. Nano Letters, 2012,12, 5287.
81 Gonzalez Z, Yus J, Sanchez-Herencia A J, et al. Journal of the European Ceramic Society, 2019,39, 366.
82 Rao K D M, Gupta R, Kulkarni G U. Advanced Materials Interfaces, 2014,1, 1400090.
83 Muzzillo C P, Reese M O, Mansfield L M. ACS Applied Materials & Interfaces, 2020,12, 25895.
84 Catrysse P B, Fan S. Nano Letters, 2010,10, 2944.
85 Jacobs D A, Catchpole K R, Beck F J, et al. Journal of Materials Che-mistry A, 2016,4, 4490.
86 Muzzillo C P. Solar Energy Materials and Solar Cells, 2017,169, 68.
87 Li B, Valverde L R, Zhang F, et al. ACS Applied Materials & Interfaces, 2017,9, 41586.
88 Pan S, Zou H, Wang A C, et al. Angewandte Chemie, 2021,59, 14942.
89 Xie J, Guo J, Wang D, et al. Advanced Materials Interfaces, 2021,8, 2000222.
90 Li Q, Jia Y, Yang X, et al. ACS Applied Materials & Interfaces, 2019,11, 31.
91 Mann D, Voogt S, Keul H, et al. Polymers, 2017,9, 475.
92 Lone S, Zhang J M, Vakarelski I U, et al. Langmuir, 2017,33, 2861.
93 Boles M A, Engel M, Talapin D V. Chemical Reviews, 2016,116, 11220.
94 Vogel N, Retsch M, Fustin CA, et al. Chemical Reviews, 2015,115, 6265.
95 Dalstein O, Gkaniatsou E, Sicard C, et al. Angewandte Chemie International Edition, 2017,56, 14011.