Materials Reports 2022, Vol. 36 Issue (Z1): 21100088-6 |
POLYMERS AND POLYMER MATRIX COMPOSITES |
|
|
|
|
|
Research Progress on Modification of Long Carbon Chain Polyamide 1012 |
ZHANG Zijian1,2, JIANG Feng1,2, YU Chunxiao2
|
1 College of Materials Science and Engineering, Donghua University, Shanghai 201620, China 2 State Key Laboratory of Biobased Fiber Manufacturing Technolegy, China Textile Academy, Beijing 100025, China |
|
|
Abstract As a long carbon chain polyamide, PA1012 has long adjacent methylene chain segments and relatively low density of amide bond and hydrogen bond, so it has the characteristics of good toughness, low crystallinity and low melting point. Akma and Evonik are major foreign manufacturers, while there are few domestic manufacturers, as well as few studies on raw materials and polymerization modification. In this paper, the related studies on the modification of PA1012 by blending and copolymerization at home and abroad are reviewed, and the effects of blending composition and ratio on the mechanical and crystallization properties of modified PA1012 are analyzed. Finally, the problems to be solved in this field have been summarized, and some ideas and suggestions for future development have been put forward.
|
Published: 05 June 2022
Online: 2022-06-08
|
|
|
|
1 Wang Y D, Zhao Q X, Liu M Y, et al. Journal of Applied Polymer Science, 2005, 98(4), 1643. 2 李馥梅. 化工新型材料, 2006(12), 6. 3 何曼君. 高分子物理, 复旦大学出版社, 2005, pp.114. 4 Bartmann M, Gude A, Droscher M, et al. EP patent, EP297245-A, 1989. 5 李勇进, 颜德岳, 朱新远, 等. 高等学校化学学报, 2000(6), 983. 6 王百木. 塑料科技, 2010, 38(3), 61. 7 李闻达, 张传辉, 肖中鹏, 等. 塑料工业, 2014, 42(11), 5. 8 万丽华, 翁志学, 黄志明, 等. 化工学报, 2004(1), 106. 9 王玉东, 刘民英, 赵清香, 等. 工程塑料应用, 2001(1), 1. 10 许冬峰, 冯新星, 张卫东, 等. 中国塑料, 2019, 33(3), 17. 11 罗玉航. 共聚酰胺6/66的制备及性能研究. 硕士学位论文, 湖南师范大学, 2017. 12 Li X H, He Y C, Dong X, et al. Polymer, 2020, 189(10), 122165. 13 苏成晓, 王道波, 张传辉, 等. 工程塑料应用, 2019, 47(11), 105. 14 李树新, 田国锋, 王朝进, 等. 中国专利, CN108003613A, 2020. 15 董侠, 朱平, 王笃金, 等. 中国专利, CN105566639A, 2016. 16 Zhu P, Dong X, Cao Y Y, et al. European Polymer Journal, 2017, 93, 334. 17 曹诣宇. 长碳链聚酰胺-聚醚多嵌段共聚物的结晶. 硕士学位论文, 中国科学院大学, 2018. 18 Wang Y, Zhu P, Lai Y, et al. Polymer, 2021, 225, 123802. 19 朱平. 长碳链聚酰胺-聚醚嵌段共聚物:合成与结构性能关系研究. 博士学位论文, 中国科学院大学, 2017. 20 Alvarez-Lainez M L, Palacio R J A, et al. Wear, 2017, 372-373, 76. 21 Wang B B,Hu G S, Zhao X. Materials Letters, 2006, 60(21-22), 2715. 22 Zierdt P, Mitzner E, Gomoll A, et al. Journal of Applied Polymer Science, 2016, 133(46), 44155. 23 Rwei S P, Tseng Y C, Chiu K C, et al. Thermochimica Acta, 2013, 55, 37. 24 Wang L L, Dong X, Wang X R, et al. Chinese Journal of Polymer Science, 2016, 38(8), 991. 25 Wu Z, Zhou C, Qi R, et al. Journal of Applied Polymer Science, 2010, 83(11), 2403. 26 Rui Y, Chen F, Iqbal M I, et al. Journal of Fiber Bioengineering and Informatics, 2018, 11(1), 41. 27 Song J, Liu J, Zhang Y, et al. Journal of Composite Materials, 2015, 49(4), 415. 28 戴军, 金惠明. 中国专利, CN100387654C, 2006. 29 许彦冰, 陈学进, 林俊澍, 等. 塑料工业, 2016, 44(11), 37. 30 陈学进, 吕广超, 许彦冰, 等. 塑料工业, 2016, 44(10), 26. 31 景新阳, 于元章. 塑料工业, 2016, 44(10), 14. 32 景新阳, 于元章. 塑料工业, 2016, 44(9), 112. 33 丁超, 梁惠强, 陈勇文, 等. 塑料工业, 2014, 42(5), 46. 34 周云霞. ACR-g-GMA增韧PA1012及其性能研究. 硕士学位论文, 长春工业大学, 2015. 35 汪永伟, 王玉东, 赵清香,等. 塑料工业, 2008, 4(1), 57. 36 胡三友. PA1212、PA1012增韧复合材料的制备及性能研究. 硕士学位论文, 郑州大学, 2014. 37 Zhou C Zhu P, Liu X, et al. Composites Part B Engineering, 2020, 206, 108539. 38 戴军, 金惠明, 任进科, 等. 中国专利, CN1502660A, 2004. |
|
|
|