Abstract Cantor alloy was first proposed by professor B. Cantor from the UK in 2004. It is a kind of high-entropy alloy which is composed of five principal elements including cobalt, chromium, iron, manganese and nickel with equal atomic ratio or close to equal atomic ratio. This alloy exhibits a single FCC structure and has four unique effects of high-entropy alloys, including high-entropy effect in thermodynamics, lattice distortion effect in structure, hysteresis diffusion effect in dynamics and cocktail effect in performance. Based on these four effects, Cantor alloy has excellent mechanical properties, wear resistance, corrosion resistance and ductility. Especially, it shows good fracture toughness and tensile strength at low temperature, which makes it the most promising material in the future.
In this paper, the four unique effects of high-entropy alloys are briefly introduced, and the common preparation methods are compared with a summary of advantages and disadvantages of different methods. Among them, vacuum arc melting coupled with copper mold casting, the most commonly used method for Cantor alloy, is discussed in detail. The evaluation of mechanical properties with temperature of Cantor alloy is summarized. Both the tensile strength and elongation gradually increase with temperature decreasing, which is benefited from the formation of nano twins. The fault energy of Cantor alloy will decrease at low temperature and consequently the twins are easily to form, resulting in the change of deformation mechanism from dislocation slip to nano twins. However, the mechanical properties of Cantor alloy at high temperature are relatively poor. Also, the yield strength of Cantor alloy at room temperature is less than 300 MPa, which is insufficient for applications as candidate structu-ral materials.
Then research works concerning about the improvement of mechanical properties of Cantor alloy are summarized, including severe plastic deformation and introduction of dispersion particles, both of which aim to improve mechanical properties by grain refinement. According to the research results, Cantor alloys exhibit stable FCC structure when the annealing temperature is higher than 1 073 K, while different kinds of precipitates will form during annealing when the temperature is lower than 1 073 K. Finally, the prospect development is given based on the above summarization of recent development results in Cantor alloys.

Key words： Cantor alloy crystal structure mechanical properties structural stability

Published: 25 January 2022 Online: 2022-01-26

CLC number:

TG146.4+18

Fund:National Natural Science Foundation of China (51901005) and the National Key Research and Development Project (2018YFC1901705).

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	PANG Baolin
	WANG Man
	XI Xiaoli

Cite this article:

PANG Baolin,WANG Man,XI Xiaoli. Research Development of Mechanical Properties and Microstructure Stability of Cantor Alloys[J]. Materials Reports, 2022, 36(2): 20080242-5.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.20080242 OR http://www.mater-rep.com/EN/Y2022/V36/I2/20080242

1 Chen J, Yao Z, Wang X, et al. Materials Chemistry and Physics, 2018, 210, 136.
2 Yeh J W, Chen S K, Lin S J, et al. Advanced Engineering Materials, 2004, 6(5), 299.
3 Cantor B, Chang I T H, Knight P, et al. Materials Science and Enginee-ring: A, 2004, 375, 213.
4 Bracq G, Laurent-Brocq M, Perriere L, et al. Acta Materialia, 2017, 128, 327.
5 He J Y, Liu W H, Wang H, et al. Acta Materialia, 2014, 62, 105.
6 Ranganathan S. Current Science, 2003, 85(10), 1404.
7 Li M J, Dong Y H, Zhang R Q, et al. Aviation Manufacturing Technology, 2019, 62(22), 58 (in Chinese).
李梦娇,董应虎,张瑞卿,等.航空制造技术, 2019, 62(22), 58.
8 Tian M B. Introduction to materials science, Tsinghua University Press, China, 2015 (in Chinese).
田民波. 材料学概论. 清华大学出版社, 2015.
9 Guo W J. Microstructure and properties of mechanically alloyed NbMoTaW(V) high melting point high entropy alloy. Master's Thesis, South China University of Science and Engineering, China, 2016 (in Chinese).
郭文晶.机械合金化NbMoTaW(V)高熔点高熵合金的组织及其性能. 硕士学位论文, 华南理工大学, 2016.
10 Xu S, Huang Y B, Liu Q, et al. Electroplating and Finishing, 2019, 38(11), 0536 (in Chinese ).
许诠, 黄燕滨, 刘谦, 等. 电镀与涂饰, 2019, 38(11), 0536.
11 Fu W J. Low temperature deformation behavior of CrMnFeCoNi high entropy alloys. Master's Thesis, Harbin Institute of Technology, China, 2019 (in Chinese).
付武靖.CrMnFeCoNi高熵合金的低温变形行为. 硕士学位论文, 哈尔滨工业大学, 2019.
12 Hu Y X, Shuang S Y, Wang B, et al. Chinese Journal of Solid Mecha-nics. 2020, 254(1-17), 1 (in Chinese).
胡远啸, 双思垚, 王冰, 等. 固体力学学报, 2020, 254(1-17), 1.
13 Won J W, Lee S, Park S H, et al. Journal of Alloys and Compounds, 2018, 742, 290.
14 Sun S J, Tian Y Z, Lin H R, et al. Journal of Alloys and Compounds, 2019, 806, 992.
15 Tirunilai A S, Sas J, Weiss K P, et al. Journal of Materials Research, 2018, 33(19), 3287.
16 Stepanov N, Tikhonovsky M, Yurchenko N, et al. Elsevier Ltd, 2015, 59, 8.
17 Sun S J, Tian Y Z, Lin H R, et al. Materials Science & Engineering A, 2019, 740, 336.
18 Otto F, Dlouhy A, Somsen C, et al. Acta Materialia, 2013, 61, 5743.
19 Xiang S, Luan H, Wu J, et al. Journal of Alloys and Compounds, 2019, 773, 387.
20 Fu W, Zheng W, Huang Y, et al. Materials Science and Engineering: A, 2020, 789, 139579.
21 Ai M E, Xiang S, Le G M, et al. Transactions of Materials and Heat Treatment, 2020, 41(3), 70 (in Chinese).
阿卜杜喀迪尔·艾麦尔, 向硕, 乐国敏, 等. 材料热处理学报, 2020, 41(3),70.
22 Gludovatz B, Hohenwarter A, Catoor D, et al. Science, 2014, 345, 1153.
23 Thurston K V S, Gludovatz B, Hohenwarter A, et al. Intermetallics, 2017, 88, 65.
24 Thurston K V S, Gludovatz B, Yu Q, et al. Journal of Alloys and Compounds, 2019, 794, 525.
25 Zhang Z, Mao M M, Wang J, et al. Nature Communication, 2015, 6, 10143.
26 Laplanche G, Kostka A, Horst O M, et al. Acta Materialia, 2016, 118, 152.
27 Stepanov N D, Shaysultanov D G, Yurchenko N Y, et al. Materials Science and Engineering: A, 2015, 636, 188.
28 Gludovatz B, George E P, Ritchie R O. JOM, 2015, 67(10), 2262.
29 He J Y, Zhu C, Zhou D Q, et al. Intermetallics, 2014, 55, 9.
30 Heczel A, Kawasaki M, Lábár J L, et al. Journal of Allays and Compounds, 2017, 711, 143.
31 Xiong F, Fu R D, Li Y J, et al. Journal of Alloys and Compounds, 2020, 822, 153512.
32 Klimova M V, Semenyuk A O, Shaysultanov D G, et al. Journal of Alloys and Compounds, 2019, 811, 152000.
33 Cai J H, Du H, Xu L P, et al. Special Casting & Nonferrous Alloys, 2019, 39(1), 1240 (in Chinese)
蔡嘉洪, 杜辉, 徐丽萍, 等. 特种铸造及有色合金, 2019,39(1), 1240.
34 Vaidya M, Guruvidyathri K, Murty B S. Journal of Alloys and Compounds, 2019, 774, 856.
35 Vaidya M, Karati A, Marshal A, et al. Journal of Alloys and Compounds, 2019, 770, 1004.
36 Liu W H, Wu Y, et al. Scripta Materialia, 2013, 68, 526.
37 Schuh B, Mendez-Martin F, Völker B, et al. Acta Materialia, 2015, 96, 258.
38 Pickering E J, Muñoz-Moreno R, Stone H J, et al . Scripta Materialia, 2016, 113, 106.
39 Otto F, Dlouhy A, Pradeep K G, et al. Acta Materialia, 2016, 112, 40.
40 Zhang T C, Li J K, Wang X B. Heat Treatment of Metals. 2018, 43(9), 10 (in Chinese).
张太超, 李俊魁, 王旭彪.金属热处理, 2018, 43(9), 10.
41 Laplanche G, Berglund S, Reinhart C, et al. Acta Materialia, 2018, 161, 338.
42 Ye F, Jiao Z, Yuan Y. Materials Chemistry and Physics, 2019, 236, 121801.
43 Park N, Lee B J, Tsuji N. Journal of Alloys and Compounds, 2017, 719, 189.
44 Klimova M V, Shaysultanov D G, Chernichenko R S, et al. Materials Science and Engineering: A, 2019, 740, 201.