多晶CoNiCrFeMn高熵合金塑性变形原子尺度分析

doi:10.11896/cldb.20110154

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (7468KB)
Export: BibTeX | EndNote (RIS)

Abstract CoNiCrFeMn high-entropy alloy plays an extremely significant role in national major fields such as deep-sea detection in lower temperature, supersonic engine and space ultrasonic motor due to its excellent properties of high strength and toughness, wear resistance, corrosion resistance, high temperature softening and low temperature resistance. Therefore, it is of great significance to research its evolution process of plastic deformation. This work focused on the basic research of the correlation characteristic for CoNiCrFeMn high-entropy alloy between load versus depth curve and micro-structural evolution, and the mechanism features of its plastic defor-mation was revealed. It was noted that the amorphous phase transition and dislocation nucleation appeared simultaneously after elastic deformation, and then increase gradually as indentation depth increases. Furthermore, an interesting phenomenon of dislocation slip can be discovered in grain, which was expected to the stress concentration induced from local contact area. At the same time, the grain boundary prevents dislocation slip. As amorphous phase transition reached the grain boundary, it will not continue. Instead, the local stress concentration was released in adjacent grains with a form of dislocation emission, so that the grain boundary becomes the source of dislocation emission. On the other hand, this report showed that the load versus depth curve during elastic stage was not sensitive to temperature changes at room temperature 300 K or below, while the load at plastic stage decreases gradually with temperature increasing. Moreover, the fluctuation degree on upper surface of poly-crystalline high-entropy alloy became serious and presented heterogeneity on the both sides of local contact area due to increasing temperature. This research will provide insight on response of the micro-structure evolution induced by loading for poly-crystalline high-entropy alloy at atomic scale, which shows an important academic value on deep exploration into the plastic deformation mechanism for poly-crystalline high-entropy alloys, and provides a reference value on improving their structure and mechanical properties.

Key words： CoNiCrFeMn high entropy alloy nano-indentation molecular dynamics plastic deformation

Published: 25 December 2021 Online: 2021-12-27

CLC number:	TG146.21
	TB383.1

Fund:This project was financially supported by Science and Technology Plan of Jiangxi Education Department (GJJ209402), the Natural Science Foundation of Fujian Province (2017J01709, 2018J01509), and the Major Project of Ningde Normal University (2017ZDK19).

About author: Weiling Huangis a lecturer with a master's degree at Gannan University of Science and Technology. She comes from Shicheng county in Jiangxi province. Her main research focus on microscopic contact deformation behavior for mechanical surface and its interface.

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	HUANG Weiling
	CHEN Jingjing

Cite this article:

HUANG Weiling,CHEN Jingjing. Atomic Mechanism of Plastic Deformation for Poly-crystalline CoNiCrFeMn High Entropy Alloy[J]. Materials Reports, 2021, 35(24): 24107-24112.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.20110154 OR http://www.mater-rep.com/EN/Y2021/V35/I24/24107

1 Li C, Xue Y, Hua M, et al. Material & Design, 2016, 90(9),601.
2 Wang F J, Zhang Y, Chen G L. Journal of Alloys and Compounds, 2009, 478(1),321.
3 Song H, Tian F, Hu Q M, et al. Physical Review Materials, 2017, 1(2),023404.
4 Sun S J, Tian Y Z, Lin H R, et al. Material Science Engineering A, 2018, 712(1),603.
5 Juan C C, Tsai M H, Tsai C W, et al. Material Letters, 2016, 184(1),200.
6 Seol J B, Bae J W, Li Z, et al. Acta Materialia, 2018, 151(1),366.
7 Li J, Fang Q H, Liu B, et al. Acta Materialia, 2018,147(1),35.
8 Mehran B, Reza T M, Dermot B. International Journal of Mechanical Sciences, 2020, 171(5),105389.
9 Iyad A A, Carlos, Eduardo M B, et al. Journal of Alloys and Compounds, 2019, 803(12),618.
10 Otto F, Dlouhy A, Somsen C, et al. Acta Materialia, 2013,61(15),5743.
11 Laplanche G, Kostka A, Horst O M, et al. Acta Materialia, 2016, 118(8),152.
12 He J Y, Zhu C, Zhou D Q, et al. Intermetallics, 2014, 55(2),9.
13 Dong B, Wang X M, Zhu Z L. Journal of Atomic and Molecular Physics, 2020,37(4),591(in Chinese)
董斌, 王雪梅, 朱子亮.原子与分子物理学报, 2020, 37(4),591.
14 Tian Y Y, Fang Q H, Li J. Nanotechnology, 2020, 31(46),1.
15 Fang Q H, Chen Y, Li J, et al. International Journal of Plasticity, 2019, 114 (6),161.
16 Sun S J, Tian Y Z, Lin H R, et al. Material Science Engineering A, 2018, 712(1),603.
17 Chen J J, Hu H J, Lai L F. Surface Technology,2018,47(8),170(in Chinese).
陈晶晶,胡洪钧,赖联锋. 表面技术, 2018, 47(8),170.
18 Chen J J, Hu H J, Li B Z. Surface Technology, 2017,46(8),195(in Chinese).
陈晶晶,胡洪钧, 李保震. 表面技术, 2017, 46(8),195.
19 Plimpton S. Journal of Computational Physics, 1995, 117(1),1.
20 Guo J, Chen J J, Wang Y Q. Ceramics International, 2020, 46(8),12686.
21 Sun S, PengX H, Xiang H G.Ceramics International, 2017,43(1),16313.
22 Xiang H G, Li H T, Fu T, et al. Acta Materialia, 2017, 138 (12),131.
23 Verlet L. Health Physics,1967, 22(1),79.
24 Jianwei X, Chuang D. Materials Science & Engineering A, 2020, 793 (12),139853.
25 Qian Y, Shang F, Wan Q. Journal of Applied Physics, 2018, 24(11),115102.
26 Qian Y, Shang F, Wan Q. Computer Material Science, 2018, 149(15),230.
27 Goel S, Luo X, Reuben R L. Applied Physical Letter, 2012, 100(23),231.
28 Goel S, Beake B, Chan C, et.al. Material Science Engineering A, 2015, 627(11), 249.