静轴肩搅拌摩擦焊2A14-T4铝合金T形接头的组织和性能

doi:10.11896/cldb.21010201

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (13707KB)
Export: BibTeX | EndNote (RIS)

Abstract 2A14-T4 aluminum alloy T joint with a thickness of 8.5 mm was connected by stationary shoulder friction stir welding (SSFSW). The weld formability, microstructures and mechanical properties of T joint were studied. The results showed that the smooth surface with small flash could be obtained and no defects were found in SSFSW welds. The cross section morphology of SSFSW-T joint presents an “open dumbbell” with both ends wide and middle narrow. Recrystallization occurred and the grain size decreased obviously in the weld nugget zone (WNZ). The average grain size was the largest in the second weld nugget zone (WNZ2), followed by the weld nugget overlap zone (WNOZ) and the smallest grains were in the first weld nugget zone (WNZ1). The recrystallization mechanism in WNZ is mainly geometric dynamic recrystallization (GDRX) and partially continuous dynamic recrystallization (CDRX). The thermo-mechanically affected zone (TMAZ) is narrow and the grains were elongated. And the grain coarsening occurred in heat affected zone (HAZ). During the welding process, the second phase particles were precipitated and coarsened, resulting in the decreasing hardness of WNZ. The fracture locations of T joint bottom plate and reinforcement plate were in the lowest hardness zone located in the borderline between TMAZ and HAZ and stress concentration locations in tensile test, respectively. Tear ridge and deformation dimples of different sizes could be observed in the fracture surface. And the second phase particles appear in the dimples, showing the characteristics of ductile fracture.

Key words： 2A14-T4 aluminum alloy SSFSW T joint microstructure mechanical property

Published: 12 November 2021

CLC number:

TG457.14

Fund:Key National Defense Basic Research Project (JCKY2017203B066).

Corresponding Authors: zhouli@hitwh.edu.cn

About author:: Haifeng Yang, Ph.D. candidate, studying in Harbin Institute of Technology (HIT), focusing on the research of friction stir weld technology in light alloys.
Li Zhou received his Ph.D. degree in materials processing engineering from Harbin Institute of Technology (HIT) in 2010. He is currently an associate professor in Harbin Institute of Technology at Weihai and participates in the development of friction stir weld equipment and technology. His research interest is friction stir weld technology of light alloys.

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	YANG Haifeng
	ZHAO Hongyun
	XU Xinxin
	SUN Guangda
	ZHOU Li
	ZHAO Huihui
	LIU Huijie

Cite this article:

YANG Haifeng,ZHAO Hongyun,XU Xinxin, et al. Microstructure and Properties of 2A14-T4 Aluminum Alloy T Joint by SSFSW[J]. Materials Reports, 2021, 35(20): 20045-20051.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.21010201 OR http://www.mater-rep.com/EN/Y2021/V35/I20/20045

1 Lu X, Tang Z Y, Lei Y P, et al. Rare Metal Materials and Engineering,2009,38(a03),223(in Chinese).
刘昕,唐振云,雷永平,等.稀有金属材料与工程,2009,38(a03),223.
2 Yang H F, Xu X X, Guo Z S, et al. Welding Joining,2019(3),12(in Chinese).
杨海峰,许欣欣,郭孜颂,等.焊接,2019(3),12.
3 Qi J F, Niu Z, Zhang D Y, et al.Chinese Journal of Lasers,2008,35(2),297.
4 Hu B, Richardson I M. Materials Science & Engineering A,2007,459(1-2),94.
5 Ma Z Y, Sharma S R, Mishra R S. Materials Science & Engineering A,2006,433(1-2),269.
6 Fratini L, Buffa G, Shivpuri R. Materials & Design,2009,30(7),2435.
7 Cui L, Yang X, Zhou G, et al. Materials Science & Engineering A,2012,543,58.
8 Threadgill P L, Leonard A J, Shercliff H R, et al. International Materials Reviews,2009,54(2),49.
9 Rai R, De A, Bhadeshia H K D H, et al. Science & Technology of Wel-ding & Joining,2011,16(4),325.
10 Acerra F, Buffa G, Fratini L, et al. International Journal of Advanced Manufacturing Techno-logy,2010,48(9-12),1149.
11 Buffa G,Fratini L, Arregi B, et al. International Journal of Material Forming,2010,3(S1),1039.
12 Cui L, Yang X, Xie Y, et al. Materials & Design,2013,51,161.
13 Hou X P, Yang X Q, Cui L, et al. The Chinese Journal of Nonferrous Metals,2013,23(11),3048(in Chinese).
侯晓鹏,杨新岐,崔雷,等.中国有色金属学报,2013,23(11),3048.
14 Fratini L, Micari F, Squillace A, et al. Key Engineering Materials,2007,344(2),751.
15 Zhao Y, Zhou L L, Wang Q Z, et al. Materials & Design,2014,53(1),106.
16 Russell M J, Threadgill P L, Thomas M J, et al. In: Conference Record of the 2008 7th World Conference on Friction Stir Welding. Kyoto, Japan,2008,pp.1095.
17 Davies P S, Wynne B P, Rainforth W M, et al. Metallurgical and Materials Transactions A,2011,42(8),2278.
18 Penalva M L, Otaegi A, Pujana J, et al. In: Conference Record of the 1st International Joint Symposium on Joining and Welding. Osaka, Japan,2013,pp.477.
19 Gascoyne J S. A microstructural investigation into the stationary shoulder corner friction stir welding of aluminium alloys. Ph.D. Thesis, The University of Sheffield, UK,2014.
20 Sun T, Roy M J, Strong D, et al. Journal of Materials Processing Techno-logy,2018,263,256.
21 Ji H, Xu M, Yao J S, et al. Electric Welding Machine,2013,43(9),37(in Chinese).
吉华,徐萌,姚君山,等.电焊机,2013,43(9),37.
22 Li D, Yang X Q, Cui L, et al. Science and Technology of Welding and Joining,2015,20(8),650.
23 Hao Y F, Ma J B, Bi H S, et al. Transactions of the China Welding Institution,2019,40(7),48(in Chinese).
郝云飞,马建波,毕煌圣,等.焊接学报,2019,40(7),48.
24 Jata K V, Semiatin S L. Scripta Materialia,2000,43(8),9.
25 Su J Q, Nelson T W, Mishra R, et al. Acta Materialia,2003,51(3),713.
26 Prangnell P B, Heason C P. Acta Materialia,2005,53(11),3179.