Materials Reports 2021, Vol. 35 Issue (Z1): 352-356 |
METALS AND METAL MATRIX COMPOSITES |
|
|
|
|
|
A Review of Crack Generation and Suppression in Laser Cladding Layer |
HOU Suoxia1, REN Chengxiang1, WU Chao2, ZHAO Jiangkun1, ZHANG Duo1, ZHANG Haoqiang1
|
1 College of Mechanical Engineering, North China University of Science and Technology, Tangshan 063210, China 2 Department of Transportation and Vehicle Engineering, Tangshan University, Tangshan 063000, China |
|
|
Abstract As a common defect in laser cladding,the cracks are seriously hindered the development and application of laser cladding. The stress causes the cracks by the different thermal expansion coefficient between the cladding layer and the substrate material after laser cladding, the element segregation in the cladding layer. It is including constraint stress, thermal stress and structural stress. In order to reduce the incidence rate of crack, it is proposed to add ceramic powder or rare earth elements into the powder, improving the parameters such as laser power and cladding speed, heat treatment of the material, and apply electromagnetic auxiliary field conditions. Analyzing the future development and research direction of crack control in cladding layer.
|
Published: 16 July 2021
|
|
Fund:National Natural Science Foundation of China (52074128). |
About author:: Suoxia Hou is the associate professor, graduate supervisor in North China University of Science and Techno-logy. She majors in surface engineering materials, the friction wear and lubrication. In the past five years, she has been a number of projects supported by the National Natural Science Foundation of China, the Provincial Natural Science Foundation of China and the Provincial Science and Technology Support Program. She has published more than 30 papers in domestic and foreign journals, including 8 SCI indexed papers, 2 monographs, and 5 invention patents.Haoqiang Zhang received his MA. Eng degree from the University of Hebei University of Polytechnic in 2005,in 2010 he received his Ph. D degree from Beijing Institute of Technology. Now he is the associate professor, graduate supervisor in North China University of Science and Technology; Deputy Director of Tangshan Nonferrous Castings Self-Lubrication Engineering Technology Research Center. In recent years, he has undertaken more than 10 scientific research projects. He has won three Tangshan Science and Technology Progress Awards, including one first prize and two third prizes, and publish more than 30 academic papers, including 5 SCI papers. |
|
|
1 Fu Fuxing, Zhang Yanli, Chang Gengrong, et al. Optik, 2016,127(1), 200. 2 李琦, 李涛, 吴祖鹏, 等.大连理工大学学报, 2020, 60(2), 159. 3 尹保健.热加工艺, 2021(4), 106. 4 Zhang J, Wu W, Zhao L. Hot Working Technology, 2013, 42, 131. 5 徐淑文,陈希章,苏传出,等.热加工工艺, 2020(22), 110. 6 陈川川. 工艺参数对激光熔覆层影响的研究. 硕士学位论文, 湖南大学, 2013. 7 Song Wulin, Echigoya J, Zhu Beidi, et al. Surface and Coatings Techno-logy, 2001,138(2-3), 291. 8 Chen Hao, Lu Yuanyuan, Sun Yunsen,et al. Surface and Coatings Technology, 2020,395, 125867. 9 杨伟,曾大新,刘建永,等.金属热处理, 2020, 45(6), 206. 10 李春燕,寇生中,赵燕春,等.功能材料, 2015, 46(7), 7025. 11 Zhang Xiaoyan, Stefan Pfeiffer, Pawel Rutkowski, et al. Applied Surface Science, 2020, 520, 146304. 12 丁阳喜,欧阳志明.材料研究与应用, 2008, 2(3), 211. 13 鲁耀钟,雷卫宁,任维彬,等.表面技术, 2020, 49(9), 233. 14 张磊,陈小明,刘伟,等.激光与光电子学进展, 2019, 56(11), 176. 15 于梦飞. Ni基合金激光熔覆层裂纹机理研究. 硕士学位论文, 中国石油大学(华东),2014. 16 焦雄,吴钢.科技信息, 2013(1), 223. 17 崔陆军,于计划,曾文涵,等.热加工工艺, DOI:10.14158.j.cnki.1001-3814.20192732. 18 曹亚男,张艳梅,揭晓华,等.热加工工艺, 2012, 41(18), 133. 19 陈翔,张德强,李金华,等.表面技术, 2021, 50(4), 113.. 20 李广琪,王丽芳,赵亮,等.热加工工艺, 2021(16), 13. 21 毛怀东. 激光熔覆层裂纹控制方法与实践. 博士学位论文. 天津大学, 2007. 22 Qi Chaoqi, Zhan Xiaohong, Gao Qiyu, et al. Optics & Laser Technology, 2019,119, 105572 . 23 Wang Chenglei, Gao Yuan, Wang Rong, et al. Journal of Alloys and Compounds, 2018, 740,1099. 24 Liu Yanan, Sun Ronglu, Niu Wei, et al. Optics and Lasers in Enginee-ring, 2019, 120, 84. 25 吕晓仁,马孝威,董丽虹,等.功能材料, 2020, 51(6), 6034. 26 陆伟. 激光熔覆高速线材轧辊熔覆层开裂问题的研究, 博士学位论文. 北京工业大学, 2006. 27 张蕾涛,张红星,刘德鑫,等.金属热处理, 2020, 45(8), 233. 28 张彦超,韦朋余,朱强,等.功能材料, 2020,51(5), 5154. 29 Song Boxue, Yu Tianbiao,Jiang Xingyu, et al. International Journal of Thermal Sciences, 2021, 159,106579. 30 Zhou Shengfeng, Zeng Xiaoyan, Hu Qianwu, et al. Applied Surface Science, 2008, 255(5), 1646. 31 李信,曲庆文,崔林.热加工工艺, 2020, 49(2), 89. 32 Alizadeh-Sh M, Marashi S P H, Ranjbarnodeh E, et al. Optics & Laser Technology, 2020, 128, 106244. 33 邓德伟,马云波,马玉山,等.金属热处理, 2020, 45(8), 113. 34 Cai Zhaobing, Cui Xiufang, Liu Zhe, et al. Optics & Laser Technology, 2018, 99, 27. 35 Hu Dengwen, Liu Yan, Chen Hui, et al. Surface and Coatings Technology, 2020, 404, 126432. 36 Quazi M M, Fazal M A, Haseeb A S M A, et al. Journal of Rare Earths, 2016, 34(6), 549. 37 Han Xing, Li Chang, Yang Yanpeng, et al.Surface and Coatings Techno-logy, 2021, 406,126750. 38 王伟,孙文磊,于江通,等.热加工工艺, 2020, 49(20), 1. 39 Sun Jiayu, Zhao Yu, Yang Lin, et al. Journal of Manufacturing Processes, 2019, 48, 51. 40 史秀梅,袁书强,依颖辉,等.精密成形工程,2012,4(6),114. 41 Hu Guofang, Yang Yong, Sun Rui, et al. Surface and Coatings Technology, 2020, 404, 126469. 42 Zhai L L, Ban C Y,Zhang J W. Optics & Laser Technology, 2019, 114, 81. |
|
|
|