烧结工艺对铜铁基含油轴承组织与性能的影响

doi:10.11896/cldb.20020028

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (8553KB)
Export: BibTeX | EndNote (RIS)

Abstract The copper-iron-based oil-impregnated bearings were prepared by powder metallurgy, and DSC, SEM, compression tests were used to study the effects of sintering atmosphere(nitrogen, decomposed ammonia and hydrogen)and sintering temperature(825—885 ℃)on the microstructure, oil content and mechanical properties of the bearing materials. The results indicate that when the samples are sintered at 865 ℃ under nitrogen atmosphere,the iron-nitrogen compound on the surface of iron powder and the oxide film on the surface of brass powder hinder the metallurgical bonding between iron powder and brass powder. When the samples are sintered under hydrogen atmosphere, severe dezincification of Cu₃Zn phase occurs. There are many irregularly shaped cracks and pores in the microstructure corresponding to these two atmospheres, which significantly reduces the oil content, hardness and crushing strength. When sintered under decompose ammonia atmosphere, the metallurgical bonding between the powder particles of the samples is sufficient, and the degree of dezincification of the Cu₃Zn phase is low. The pores tend to be spherical, and the oil content, hardness and crushing strength are significantly improved. When the samples are sintered at 825 ℃ and 845 ℃ under decompose ammonia atmosphere, no obvious metallurgical bonding occurs between the powder particles and the hardness and crushing strength are low. When the sintering temperature is increased to 865 ℃, the degree of metallurgical integration has increased, the number of pores is greatly reduced, and the hardeness and crushing strength are significantly improved. The sintering temperature is increased to 885 ℃, the sample is oversintering, the shrinkage is large, and the oil content decreases sharply. When sintered at 865 ℃ under decompose ammonia atmosphere, the sintered samples have good comprehensive properties. The oil content, hardness and crushing strength are 18.8% (volume fraction), 43.7HB, and 271.1 MPa, respectively.

Key words： powder metallurgy copper-iron-based oil-impregnated bearing sintering process crushing strength dezincification

Published: 10 May 2021

CLC number:

TB 333

Fund:National Natural Science Foundation (51474108), Science and Technology Program of Guangzhou (201807010075) and the National Natural Science Foundation of Guangdong (2018B030311051).

About author:: Dongyu Li is a master candidate in the School of Mechanical and Automotive Engineering, South China University of Technology. The research mainly focuses on copper-iron-based oil-impregnated bearings. He has participated in two Science and Technology Program of Guangzhou.
Xiaoqiang Li is a professor and doctoral supervisor of South China University of Technology. Mainly engaged in powder metallurgy, cemented carbide and dissimilar metal connection. He won one first prize of Guangdong Science and Technology Award, and one second prize of National Science and Technology Progress Award by the Ministry of Education. He has published 153 papers in academic journals.

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	LI Dongyu
	LI Xiaoqiang
	LI Jingmao
	QU Shengguan
	XU Geqing

Cite this article:

LI Dongyu,LI Xiaoqiang,LI Jingmao, et al. Effect of Sintering Process on Microstructure and Properties of Copper-Iron-based Oil-impregnated Bearing[J]. Materials Reports, 2021, 35(8): 8157-8163.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.20020028 OR http://www.mater-rep.com/EN/Y2021/V35/I8/8157

1 Li J, Liu Y, Lian L X, et al. Composites Part B:Engineering,2012,43(4),1681.
2 ünlü B S, Atik E. Journal of Alloys and Compounds,2010,489(1),262.
3 Qian Q H. Study on alloying and wear properties of P/M iron-copper based oilless bearing materials. Master's Thesis, Southeast University, China,2014(in Chinese).
秦清华.粉末冶金铁铜基含油轴承材料的合金化及摩擦磨损性能.硕士学位论文,东南大学,2014.
4 Qian H J. Effect of sintering process and alloy element on microstructure and mechanical properites of Cu-based oil-impregnated bearing. Master's Thesis, Nanjing University of Aeronautics and Astronautics, China,2016(in Chinese).
钱杭君.烧结工艺及合金元素对铜基含油轴承组织与性能的影响.硕士学位论文,南京航空航天大学,2016.
5 RaJa A, Anish U, Dinesh A. Bulletin of Materials Science,2013,36(3),447.
6 Jabur A S. Powder Technology,2013,237,477.
7 Imai H. Powder Technology,2010,198(3),417.
8 Liu J P, Yang X J, Zeng L F, et al. Journal of Nanchang University (Engineering & Technology),2014,36(4),373(in Chinese).
刘锦平,杨湘杰,曾龙飞,等.南昌大学学报:工科版,2014,36(4),373.
9 Zheng L L, Liu J X, Li S K, et al. Rate Materials,2016,35(3),242.
10 Han F L, Jia C C. Sintered metal oil bearing: principle, design, manufacturing and application, Chemical Industry Press, China,2004(in Chinese).
韩凤麟,贾成厂.烧结金属含油轴承:原理、设计、制造与应用.化学工业出版社,2004.
11 Carl L Y. Matheson gas data book, Chemical Industry Press, China,2003(in Chinese).
卡尔L.约斯.Matheson气体数据手册(原书第7版),化学工业出版社,2003.
12 Zhu H H, Lu L, Fuh J Y H. Materials Science & Engineering A,2004,371(1-2),170.
13 Zheng H N, He Y D, Xing S Y, et al. Rate Materials,2016,41(3),267.
曾慧楠,贺永东,邢诗雨,等.稀有金属,2016,41(3),267.
14 Shen P, Hu J D, Guo Z X, et al. Metallurgical and Materials Transactions A,1999,30(8),2229