Materials Reports  2020, Vol. 34 Issue (Z1): 157-160 |
| INORGANIC MATERIALS AND CERAMIC MATRIX COMPOSITES |
|
|
|
|
|
| Preparation of Annular Uranium Dioxide Fuel Pellets by Gel-casting Molding |
| MA Liang1, YANG Jing2, WANG Jiping1, XU Kui2
|
1 State Key Laboratory For Mechanical Behavior of Materials, Xi'an Jiaotong University, Xi'an 710049, China;
2 Key Laboratory for Reactor Fuel and Materials, Nuclear Power Institute of China, Chengdu 610041, China |
|
|
|
|
Abstract Annular uranium dioxide pellets have many advantages in increasing reactor power density. In this paper The Annular Uranium dioxide fuel pellets is gel-mould cast with N-methylolacry system. The influence of pH value and solid phase content on the viscosity of the slurry was stu-died. At the same time, the effect of monomer/crosslinker ratio, premix/initiator ratio on slurry gel solidification was studied. On this basis, the annular UO2 fuel pellets were prepared by gel-casting, and the green pellets were dried and sintered. The results show that when the solid content is 58vol%, pH=9.5, it can prepare high-solid content and low viscosity UO2 ceramic slurry. When the mass ratio of monomer/crosslinker is 15/1, the premix/initiator volume ratio is 100/2, gel curing processing is best. The annular pellet green body with wall thickness of 2.5 mm and 1.5 mm was prepared, and the wall thickness after sintering was 2.0 mm and 1.2 mm respectively; the indexes such as sintered density and grain size met the technical requirements.
|
|
Published: 01 July 2020
|
|
|
| About author:: Liang Ma, a postgraduate student of Xi'an Jiaotong University, he is currently mainly engaged in nuclear fuel and burnable poison pellet preparation ; Jing Yang, researcher, master tutor, graduated from Shandong University in 1989, mainly engaged in nuc-lear fuel and materials research. Published more than 10 articles as the first author. |
|
|
1 Han K H, Seo K W, Hwang D H, et al. Nuclear Engineering and Design,2006,236,2.
2 Doh J, Kim Y, Lee J. Engineering Optimization,2018,50,12.
3 Han K H, Chang S H. Nuclear Engineering and Design,2003,226,3.
4 Feng D, Hejzlar P, Kazimi M S. Nuclear Technology,2007,160,1.
5 Hastings I J. Journal of Nuclear Materials,1984,126,2.
6 Gilissen R, Erauw J P, Smolders A, et al. Materials & Design,2000,21,4.
7 Jia Y, Kanno O Y, Xie Z P. Journal of the European Ceramic Society,2002,22,12.
8 林晓亮,余阳,陈仕俊.中国陶瓷,2017(4),57.
9 曹文,谭训彦,夏光华,等.中国陶瓷,2016(11),67.
10 谭训彦,朱庆霞,虞澎澎,等.中国陶瓷,2011,47(4),7.
11 施磊,何秀兰,唐丽娜,等.材料导报:综述篇,2015,29(7),133.
12 温江波,牛敏,苏磊,等.硅酸盐学报,2019,47(9),1198. |
|
|
|
渝公网安备50019002502923号 © Editorial Office of Materials Reports.