钛合金BCC↔HCP相变的变体选择及其对晶体取向的影响

doi:10.11896/cldb.18070038

Abstract
Figure/Table
References
Related Citation (6)

Download:

Full Text ( PDF ) (17775KB)
Export: BibTeX | EndNote (RIS)

Abstract In the actual production of titanium alloys, the material is usually forged or hot processed in the β single-phase region and the α+β dual-phase region, plus a corresponding heat treatment. During the process, titanium alloys usually experienced the α?β phase transformation. In idea state, the variants randomly nucleate and grow, and fine grain and uniform orientation distribution willbe formed,which lead to good mechanical properties of materials. However, due to the existence of various factors in the actual thermal processing, the phenomenon of variant selection during phase transformation occurs, which will affect the distribution of crystal orientation and thus impair the mechanical properties of the material. To sum up, the factors influencing the selection of variants during the phase transition process can be divided into: (1) various internal defects formed in the alloy and the residual phase; (2) the influence of processing technology.
The internal defects formed during the processing of titanium alloys mainly include dislocations, various grain boundaries and phase boundaries, and inclusions. In addition to α and β titanium alloys, residual phases exist at room temperature. From a thermodynamic point of view, these defects cause the energy imbalance of the entire system. In order to balance the system energy, some variants need to be precipitated, resulting in the phenomenon of variant selection. So far, various micro-mechanism studies have found that titanium alloys tend to form adjacent β crystal grains that share the same 〈110〉 direction during the thermal processing, which usually causes α-phase to be precipitated with the c-axis parallel to β〈110〉 direction, and the frequency of the alpha-variant to be preferentially selected is very high, and the rotting cause of this β/β-crystal couple has not been clarified. In addition, the titanium alloy phase transition is very sensitive to the thermal processing parameters, such as cooling rate, processing temperature, holding time and deformation and so on, which will cause variant selection. Through in-depth analysis, the influe-nce of the processing technology on the selection of variants can ultimately be attributed to the fact that it leads to abnormalities in the internal structure of the material, which in turn leads to variant selection.
Reports of improving the mechanical properties and crystal orientation distribution of the material through controlling the selection of variants in the phase transition process have not yet appeared. The research results on the phase transformation of titanium alloys are mainly completed by developed countries, and most of the outstanding results appeared before 2010. After 2010, there are few new results. This is mainly due to the fact that it is difficult to directly obtain the information of the α?β transition at high temperature, which has become a heavy obstacle for the in-depth study of the selection of phase change variants. However, the emergence of in-situ EBSD technology in recent years has provided new opportunities for the study of this issue. It is believed that a number of new results will emerge in the coming years.
In this paper, the mechanism of thevariant selection caused by various internal and external factors in the phase transformation of titanium alloys are summarized. The relationship between the titanium alloy texture evolution and the evolution of α?β in titanium alloys is described. The current paperintroduced the essence, causes ofvariantselection, and its effects on the distribution of crystal orientation, and pointed out the current problems in the direction of the study and the future research focus.

Key words： phase transition variant selection texture evolution

Published: 23 July 2019

CLC number:

TM914.4+2

About author:: Guoming Zheng, born in 1990, graduated from University of Science and Technology Liaoning in 2014 with a bachelor's degree in engineering. Now, he is a master's degree candidate in Northeastern University andcarrying out scientific research under the guidance of teacher Mao Xiaonan. Mainly engaged in the study of TA19 titanium alloy microstructure and texture.
Xiaonan Mao,Ph.D., director of the Titanium Alloy Institute of Northwest Institute for Nonferrous Metal Research, professor of Northeastern University. Mainly engaged in material investigation of high-performance hydrogen storage, high-temperature titanium alloys used above 600 ℃ and so on. Having won provincial scientific and technological progress awards for many times and published more than 60 SCI papers.

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	ZHENG Guoming
	LI Lei
	MAO Xiaonan
	CAI Jianhua
	WU Cong
	LEI Lei

Cite this article:

ZHENG Guoming,LI Lei,MAO Xiaonan, et al. Variant Selection During Titanium Alloy BCC↔HCP Phase Transformation and Its Effect on Crystal Orientation[J]. Materials Reports, 2019, 33(17): 2910-2917.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.18070038 OR http://www.mater-rep.com/EN/Y2019/V33/I17/2910

Yi Y, Lu Y F,Ge P, et al. Material Sciences, 2014, 4(5), 197.2 Zhao Z B. The crystallographic orientation of α phase in Ti60 alloy. Ph. D. Thesis, University of Chinese Academy of Sciences, China, 2014 (in Chinese).赵子博.Ti60合金中α相的晶体取向研究. 博士学位论文,中国科学院大学,2014.3 Glavicic M G, Bartha B B, Jha S K, et al. Acta Materialia, 2012, 60(3), 1048.4 Motyka M, Kubiak K, Sieniawski J. Phase transformations and characte-rization of α+β titanium alloys, Elsevier, Netherland, 2014.5 Lonardelli I, Gey N, Wenk H R, et al. Acta Materialia, 2007, 55(17), 5718.6 Jourdan C, Gastaldi J, Marzo P, et al. Material Sciences, 1991,55(26), 4355.7 Glavicic M G, Bartha B B, Jha S K, et al. Materials Science and Engineering A, 2009, 60(3), 325.8 Bhattacharyya D, Viswanathan G B, Denkenberger R, et al.Acta Mate-rialia, 2003, 51(16), 4679.9 Shi R, Dixit V, Fraser H L, et al. Acta Materialia, 2014,23(75) ,156.10 Bocher P, Jahazi M, Germain L, et al. Solid State Phenomena, 2005,36(105), 132.11 Germain L, Gey N, Humbert M, et al.Materials Science Forum, 2005, 495,663.12 Furuhara T, Maki T.Materials Science and Engineering A, 2001, 312(1), 145.13 Xin S W,Zhao Y Q. Titanium Industry Progress, 2010(24),23(in Chinese).辛社伟, 赵永庆. 钛工业进展, 2010 (24), 23.14 Skvortsova S V, Ilyin A A.Russian Metallurgy, 2007, 2007(5), 355.15 Stanford N, Bate P S.Acta Materialia, 2004, 56(17), 5215.16 Davies P S. An investigation of microstructure and texture evolution in the near-a titanium alloy timetal 834. Ph.D. Thesis, University of Sheffield, UK, 2009.17 Ahmed T, Rack H J. Materials Science and Engineering A, 1998,25(162),206.18 Lutjering G, Williams J C. Titanium, Springer, Germany, 2003.19 Obasi G C. Variant selection and its effect on texture in Ti-6Al-4V. Ph. D. Thesis, University of Manchester, USA,2011.20 Mironov S, Murzinova M, Zherebtsov S, et al. Acta Materialia, 2009, 57(8), 2470.21 Bhattacharyya D, Viswanathan G B, Fraser H L, et al. Acta Materialia, 2007, 55(20), 6765.22 Gey N, Bocher P, Uta E, et al. Acta Materialia, 2012,63(67), 2647.23 Romero J, Preuss M, Quinta J. Acta Materialia, 2009, 57(18), 5501.24 Humbert M, Germain L, Geya N, et al.Materials Science and Engineering A, 2006, 430(1-2), 157.25 Zhao Z B, Wang Q J, Hu Q M, et al. Acta Materialia, 2017,25(126), 372.26 Lonardelli I, Gey N, Wenk H R, et al. Acta Materialia, 2007, 55(17), 5718.27 Cayron C. Scripta Materialia, 2008, 59(5), 570.28 Germain L, Gey N, Humbert M, et al.Acta Materialia,2008, 56(16), 4298.29 Germain L, Gey N, Humbert M,et al. Acta Materiaia, 2005, 53(13), 3535.30 Humbert M, Germain L, Gey N, et al.Materials Science and Engineering A, 2006, 430(1-2),157.31 Zhao Z B, Wang Q J, Liu J R, et al.Acta Materialia, 2017, 131(856), 305.32 Karthikeyan T, Dasguptaa A, Khatirkar R, et al. Materials Science and Engineering A, 2010, 528(2),549.33 Obasi G C, Birosca S, Leo P D G, et al. Acta Materialia, 2012, 60(17), 6013.34 Gey N, Humbert M. Acta Materialia, 2002, 50(2), 277.35 Zhu Z S, Gu J L, Liu R Y, et al.Materials Science and Engineering A, 2000, 112(2),199.36 Ramachandra C,Singh A K,Sarma G M K, et al. Metallurgical Transactions A, 1993, 24, 1273.37 Zeng L, Bieler T R. Materials Science and Engineering A, 2005, 392(1-2), 403.38 Stanford N, Bate P S.Materials Science Forum, 2005,495(497), 669.39 Germain L, Gey N, Humbert M. Ultramicroscopy, 2007, 107(12), 1129.40 Karthikeyan T,Saroja S, Vijayalakshmi M. Scripta Materialia, 2006, 55(9), 771.41 Seward G G E, Celotto S, Prior D J, et al.Acta Materialia, 2004, 52(4), 821.