基于内聚力模型的热障涂层失效行为研究

doi:10.11896/cldb.18030286

Abstract
Figure/Table
References
Related Citation (13)

Download:

Full Text ( PDF ) (1775KB)
Export: BibTeX | EndNote (RIS)

Abstract Thermal barrier coatings (TBCs) hold widespread applications in gas turbines and aero engines because of their excellent thermal insulation, wear and corrosion resistance, which can improve engine thermal efficiency and prolong the service life of turbine blades. Generally, the failure of thermal barrier coatings is caused by the crack propagation, and the major failure modes consist of surface cracking and interface dela-mination. Concerning the crack propagation behavior of coatings, the most important and direct research approaches is to numerically simulate the entire failure process of the thermal barrier coatings, so as to acquire deep understanding of the mechanism of coating failure.
The cohesive zone model (CZM) is capable of describing the interface cracking problem accurately, reducing or even relieving the stress singularity at the crack tip, and simulating the propagation of any crack without defining the pre-crack. When CZM is employed to simulate the process of surface cracking and interfacial delamination of the thermal barrier coatings, the cohesive unit is usually embedded between solid elements where cracks may occur. Once the material is destroyed, the cracks will form and expand along the direction of the cohesive unit. Nevertheless, the damage failure of TBCs are affected by diverse factors accompanied by complex failure mechanism. The variety of failure modes and the insufficiency of the CZM itself make CZM fail to describe the whole picture in study of thermal barrier coatings failure.
At present, the simulation of damage failure process of TBCs has been realized by CZM, including the surface cracking process and the interface layer failure process. However, the majority of current studies regard the TBCs as homogenous materials and neglect the micro-defects inside the coating. Moreover, there is still some problems in CZM itself, such as the determination of parameters. With the advance of the TBCs and CZM, and the deepening of understanding to CZM, the simulation of failure process of TBCs by the CZM has been developed and improved continuously. Regarding to the simulation of surface cracking, the CZM is embedded vertically in the ceramic coating to simulate the expansion beha-vior of the internal surface cracks in the ceramic layer. Concerning the simulation of the crack growth behavior inside the ceramic coatings, the extended finite element method is commonly adopted, while CZM is seldom used. The CZM can effectively solve the problem of interface cracking, especially the bonding layer/ceramic interface cracking problem, it is widely employed in the study of interface failure problem of TBCs.
In this article, we give a brief introduction of the CZM, summarize the progress of CZM in simulating the failure behavior of the TBCs, and finally point out problems in the current research and the future development direction.

Key words： thermal barrier coatings cohesive zone model failure behavior crack propagation surface cracking interface delaminating

Published: 08 May 2019

CLC number:

TG115.28

Fund:This work was financially supported by the National Natural Science Foundation of China (51775553,51535011), 973 Projects (61328304).

About author:: Xuehuan Li, enrolled the School of Materials Science and Engineering, Hebei University of Technology in 2016. She is a jointly cultivated graduate student of Hebei University of Technology and the National Key Laboratory for Remanufacturing, Academy of Army Armored Forces. She is currently pursuing her Master’s degree under the supervision of Prof. Guolu Li and Haidou Wang.Her research has focused on remanufacturing surface engineering. Haidou Wang, received his Ph.D. degree in Department of Mechanical Engineering from Tsinghua University in 2003. He joined the National Key Laboratory for Remanufacturing at Academy of Army Armored Forces from then on. He is a professor and the deputy director of the laboratory. His current research areas cover the surface engineering, remanufacturing and tribology, especially in service life evaluation of surface coatings and solid film lubrication.

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	LI Xuehuan
	DI Yuelan
	WANG Haidou
	LI Guolu
	DONG Lihong
	MA Yize

Cite this article:

LI Xuehuan,DI Yuelan,WANG Haidou, et al. An Overview on Failure Behavior Study of Thermal Barrier Coatings Based on Cohesive Zone Model[J]. Materials Reports, 2019, 33(9): 1500-1504.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.18030286 OR http://www.mater-rep.com/EN/Y2019/V33/I9/1500

1 Padture N P, Gell M, Jordan E H. Science,2002,296(5566),280.
2 Marino K A, Hinnemann B, Carter E A. Proceedings of the National Academy of Sciences of the United States of America,2011,108(14),5480.
3 Bäker M, Seiler P. Journal of Thermal Spray Technology,2017,26(6),1146.
4 Yang L, Zhou Y C, Lu C. Acta Materialia,2011,59(17),6519.
5 Wang L, Ni J X, Shao F, et al. Journal of Thermal Spray Technology,2017,26(1-2),116.
6 Yang Li. Nondestructive evaluation of oxidation, damage and fracture of thermal barrier coatings. Ph.D. Thesis, Xiangtan University, China,2007(in Chinese).
杨丽.热障涂层氧化、损伤与断裂的无损评价研究.博士学位论文,湘潭大学,2007.
7 Zhou Y C,Liu Q X,Yang L,et al. Acta Mechanica Solida Sinica,2010,31(5),504(in Chinese).
周益春,刘奇星,杨丽,等.固体力学学报,2010,31(5),504.
8 Jin G H, Damage and failure analysis of heterogeneous materials based on cohesive zone model. Master’s Thesis, Zhejiang University of Technology,China,2015(in Chinese).
靳国辉.基于内聚力模型非均质材料损伤与失效的数值研究.硕士学位论文,浙江工业大学,2015.
9 Gu Z P, Study on delamination failure mechanism of composite laminates based on cohesive theory. Master’s Thesis, Zhejiang University, China,2016(in Chinese).
顾志平.基于内聚力理论的复合材料分层失效机理研究.硕士学位论文,浙江大学,2016.
10Mcgarry J P, Éamonn Ó Máirtín, Parry G, et al. Journal of the Mechanics & Physics of Solids,2014,63(1),336.
11Éamonn Ó Máirtín, Parry G, Beltz G E, et al. Journal of the Mechanics & Physics of Solids,2014,63(1),363.
12Huang L G. The analysis of cohesive zone model and user-defined subroutine development in finite element method. Master’s Thesis, Zhengzhou University,China,2010(in Chinese).
黄刘刚.内聚力模型的分析及有限元子程序开发.硕士学位论文,郑州大学,2010.
13Dugdale D S. Journal of the Mechanics & Physics of Solids,1960,8(2),100.
14Barenblatt G I. Advances in Applied Mechanics,1962,7,55.
15Li Zhuo,The application of CZM and XFEM methods on crack propagation simulation. Master’s Thesis, Guangxi University, China,2013(in Chinese).
李卓.内聚力和扩展有限元方法在裂纹扩展模拟中的应用研究.硕士学位论文,广西大学,2013.
16Sun J Q, Ji D M, Tan J Z, et al. Journal of Shanghai University of Electric Power,2016,32(2),129(in Chinese).
孙家啟,纪冬梅,唐家志,等.上海电力学院学报,2016,32(2),129.
17Zhou M, Yao W B, Yang X S, et al. Surface & Coatings Technology,2014,240(7),40.
18Yang L, Zhou Y C, Mao W G, et al. Applied Physics Letters,2008,93(23),299.
19Biaas M, Majerus P, Herzog R, et al. Materials Science & Engineering A,2005,412(1-2),241.
20Yang X S. Finite element analysis of failure process of thermal barrier coatings by using cohesive element. Master’s Thesis, Xiangtan University, China,2013(in Chinese).
杨雪松.基于内聚力单元热障涂层体系失效过程有限元模拟分析.硕士学位论文,湘潭大学,2013.
21Wang L, Li D C, Yang J S, et al. Journal of the European Ceramic Society,2016,36(6),1313.
22Yang X S, Wan J, Dai C Y, et al. Surface & Coatings Technology,2013,223(52),87.
23Fan X L, Xu R, Zhang W X, et al. Applied Surface Science,2012,258(24),9816.
24Fan X, Zhang W, Wang T, et al. Applied Surface Science,2011,257(15),6718.
25Wang L, Yang J S, Ni J X, et al. Surface & Coatings Technology,2016,285,98.
26Fleck N A, Cocks A C F, Lampenscherf S. Journal of the European Ceramic Society,2014,34(11),2687.
27Moridi A, Azadi M, Farrahi G H. Surface & Coatings Technology,2014,243(4),91.
28Wang L, Zhao Y X, Zhong X H, et al. Journal of Thermal Spray Technology,2014,23(3),431.
29Vermaak N, Michailidis G, Estevez R, et al. Structural & Multidisciplinary Optimization,2014,50(4),623.
30Nordhorn C, Mücke R, VaBen R. Surface & Coatings Technology,2014,258,181.
31Aleksanoglu H, Scholz A, Oechsner M, et al. International Journal of Fatigue,2013,53(7),40.
32Wu D J, Mao W G, Zhou Y C, et al. Applied Surface Science,2011,257(14),6040.
33Chen Z B, Wang Z G, Zhu S J. Surface & Coatings Technology,2011,205(15),3931.
34Yao W B, Dai C Y, Mao W G, et al. Surface & Coatings Technology,2012,206(18),3803.
35Qian L, Zhu S, Kagawa Y, et al. Surface & Coatings Technology,2003,173(2-3),178.
36Zhu W, Yang L, Guo J W, et al. Applied Surface Science,2014,315(315),292.
37Zhu W, Yang L, Guo J W, et al. In: National Physical and Mechanical Conference. Xiangtan,2014,pp.76.
38Yang L, Zhong Z C, You J, et al. Surface & Coatings Technology,2013,232(10),710.
39Yang L, Zhong Z C, Zhou Y C, et al. Journal of Mechanics,2016,32(2),1.
40Guo S, Kagawa Y. Scripta Materialia,2004,50(11),1401.
41Xia S Q. The research of the crack propagation in thermal spray remanufacturing product. Master’s Thesis, Beihang University, China, 2016(in Chinese).
夏世琦.热喷涂再制造件的裂纹扩展行为研究.硕士学位论文,北京航空航天大学,2016.
42Leo C V D, Luk-Cyr J, Liu H, et al. Acta Materialia,2014,71(1),306.
43Hille T S, Suiker A S J, Turteltaub S. Engineering Fracture Mechanics,2009,76(6),813.
44Yao W B, Dai C Y, Mao W G, et al. Surface & Coatings Technology,2012,206(18),3803.
45Qian L, Zhu S, Kagawa Y, et al. Surface & Coatings Technology,2003,173(2-3),178.
46Zhu W, Yang L, Guo J W, et al. Applied Surface Science,2014,315(315),292.
47Chen X, Hutchinson J W, He M Y, et al. Acta Materialia,2003,51(7),2017.
48Busso E P, Wright L, Evans H E, et al. Acta Materialia,2007,55(5),1491.
49Wang L, Fan Q, Liu Y, et al. Materials & Design,2015,86,89.
50Bialas M. Surface & Coatings Technology,2008,202(24),6002.