激光熔覆制备硬质颗粒增强镍基合金复合涂层的研究进展

doi:10.11896/cldb.18020081

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (2739KB)
Export: BibTeX | EndNote (RIS)

Abstract For the sake of satisfying diverse service conditions, many engineering components should be equipped with excellent surface properties, such as high hardness, good wear resistance and corrosion resistance. Ordinary metal material can achieve improved surface properties by cladding the alloy powders on its surface. The laser cladded coating holds favorable adhesion property, excellent microstructure, small heat affec-ted zone and outstanding mechanical properties. The commonly used laser cladding approaches primarily include preset powder method and synchronous powder feeding.
The common cladding materials are mainly divided into three categories, namely Fe, Co and Ni based. The Fe-based coatings feature high hardness and wear resistance, and lower price as well. Nevertheless, the Fe-based coating is prone to produce defects during the preparation process, resulting in the decline in performance and reliability of the coating. Co-based coatings hold excellent high temperature resistance and corrosion resistance, yet their mechanical properties are poor and the price is extremely high, which seriously blocks their widespread application in industry. Ni-based coatings possess excellent wear resistance, good toughness and wettability, and their production cost is relatively economical, which show broad application prospects. In recent years, great efforts have been put into the research of Ni-based coating.
At present, the commonly used approach for strengthening Ni based coatings include adjusting the process parameters of laser cladding and adding hard phases or appropriate elements to the Ni based coatings. Many researchers have concentrated on optimizing the composition of Ni-based alloy powders, that is, adding hard phases or appropriate elements to Ni based powders to enhance the properties of the Ni coating. The major hard phase particles added to Ni based coatings include WC, NbC, TiC, TaC and VC. Attempts that adding certain compound elements to assist the generation of reinforcing phases in laser cladding process by in-situ reaction have been made by researchers. For instance, the addition of pure Nb powder (or Nb₂O₅) and graphite powder contribute to generate NbC, the addition of pure Ti powder and graphite powder is conducive for the formation of TiC by in-situ reaction. Some researchers have tried to introduce a single element including Nb, Ti, Al, Ta and so on, in order to improve the performance of the coating. Besides, the effect of rare earth elements on the properties of coatings have been explored as well.
Ni-based alloy coating prepared by laser cladding are endowed with high bonding strength, excellent corrosion resistance and wear resistance, exhibiting a broad application prospect in engineering. The mechanical properties of the coatings can be further enhanced by improving the composition of the alloy powders. In this article, the research progress of hard particle reinforced Ni-based alloy composite coatings is reviewed. The problems that need to be solved for the hard particle-reinforced nickel-based alloy coatings are pointed out, and the prospects of the research are also discussed.

Key words： laser cladding Ni-based alloy microstructure mechanical property

Published: 10 May 2019

CLC number:

TG174.44

Fund:This work was financially supported by the National Natural Science Foundation of China (51775006).

About author:: Xuelong Ping, he is a graduate student in School of Materials and Engineering, Beijing University of Technology. At present, the main research is laser surface modification of materials.Hanguang Fu, male, born in 1964. Researcher and doctoral tutor at the School of Materials Science and Engineering, Beijing University of Technology. He has been engaged in the research of advanced wear-resistant materials for a long time, especially in large metallurgical roll solidification and heat treatment, high-strength and toughness wear-resistant composite castings and high-boron wear-resistant alloys. He has won two se-cond-class awards for technical invention, two second-class awards for scientific and technological progress, and six first-class awards at the provincial and ministerial levels. There are 83 patents authorized for invention, 4 monographs published, 260 papers published, and more than 190 articles included in SCI and EI.

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	PING Xuelong
	FU Hanguang
	SUN Shuting

Cite this article:

PING Xuelong,FU Hanguang,SUN Shuting. Progress in Preparation of Hard Phase Reinforced Ni-based Alloy Composite Coating by Laser Cladding[J]. Materials Reports, 2019, 33(9): 1535-1540.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.18020081 OR http://www.mater-rep.com/EN/Y2019/V33/I9/1535

1 Sharma S P, Dwivedi D K, Jain P K. Wear,2009,267(5-8),853.
2 Chaliampalias D, Vourlias G, Pavlidou E, et al. Surface Science,2009,255(6),3605.
3 Zhang J, Hu Y, Tan X J, et al. Chinese Journal of Nonferrous Metals,2015,25(5),1525.
4 Wang P Z, Qu J X, Shao H S, et al. Materials and Design,1996,17(5-6),289.
5 Bansal A, Zafar S, Sharma A K, et al. Journal of Materials Engineering and Performance,2015,24(10),1.
6 Wang S L, Zhang Z Y, Gong Y B, et al. Journal of Alloys and Compounds,2017,728,1116.
7 Quazi M M, Fazal M A, Haseeb A S M A, et al. Journal of Rare Earths,2016,34(6),550.
8 Paul C P, Mishra S K, Tiwari P, et al. Optics and Laser Technology,2013,50,155.
9 Ortiz A, García A, Cadenas M, et al. Surface and Coatings Technology,2017,324,298.
10 Ma Q S, Li Y J, Wang J, et al. Journal of Alloys and Compounds,2015,645,151.
11 Tobar M J, álvarez C, Amado J M, et al. Surface and Coatings Technology,2006,200,6313.
12 Guo C, Chen J M, Zhou J S, et al. Surface and Coatings Technology,2012,206,2064.
13 Zhou S F, Lei J B, Dai X Q, et al. International Journal of Refractory Metals and Hard Materials,2017,64,234.
14 Li F Q, Feng X Y, Chen Y B. Chinese Journal of Lasers,2016,43(4),0403009-1(in Chinese).
李福泉,冯鑫友,陈彦宾.中国激光,2016,43(4),0403009-1.
15 Zang C C, Wang Y Y, Zhang Y D, et al. Rare Metal,2019,39(5),385(in Chinese).
臧春城,王延忠,张以都,等.稀有金属,2019,39(5),385.
16 Matthews S, James B, Hyland M. Surface and Coatings Technology,2013,70,203.
17 Lou D Y, He C L, Shang S, et al. Materials Letters,2013,93,304.
18 Yu J, Zhu L, Luo L M, et al. Hot Working Technology,2010,39(6),86(in Chinese).
俞佳,朱流,罗来马,等.热加工工艺,2010,39(6),86.
19 Zhang D W, Lei T C, Li F J. Wear,2001,251,1372.
20 Zhang D W, Lei T C. Wear,2003,255(1-6),129.
21 Zhang D W, Zhang X P. Surface and Coatings Technology,2005,190(2),212.
22 Wilson J M, Shin Y C. Surface and Coatings Technology,2017,207(9),517.
23 Jiang D, Hong C, Zhong M, et al. Surface and Coatings Technology,2014,249(7),125.
24 Shen M Y, Tian X J, Liu D, et al. Journal of Alloys and Compounds,2018,734,188.
25 Xu X, Mi G Y, Xiong L D, et al. Journal of Alloys and Compounds,2018,740,16.
26 Ikeno S, Furuta K, Matsuda K J. Journal of Japan Institute of Light Metals,1995,45(5),249.
27 Chao M J, Niu X, Yuan B, et al. Surface and Coatings Technology,2006,201,1102.
28 Rajab F H, Liu Z, Li L. Applied Surface Science,2018,427,1135.
29 Lu W J, Zhang D, Zhang X N, et al. Materials Science and Engineering A,2001,311,142.
30 Du J N, Dong G, Deng Q L, et al. Applied Laser,2012(4),277(in Chinese).
杜竞楠,董刚,邓琦林,等.应用激光,2012(4),277.
31 Niu X, Chao M J, Wang W L, et al. Chinese Journal of Lasers,2006,33(7),987.
32 Cao Y B, Zhi S X, Gao Q, et al. Materials Characterization,2016,119,159.
33 Wu X L. Surface and Coatings Technology,1999,115,111.
34 Chao M J, Wang W L, Liang E J, et al. Surface and Coatings Technology,2008,202(10),1918.
35 Moghaddam E G, Karimzadeh N, Varahram N, et al. Materials Science and Engineering A,2013,585(22),422.
36 Zhao G L, Huang C Z, Liu H L, et al. International Journal of Refractory Metals and Hard Materials,2013,36,122.
37 Wang Z T, Zhou X H, Zhao G G. Transactions of Nonferrous Metals Society of China,2008,18(4),831.
38 Li M, Huang J, Zhu Y Y, et al. Surface and Coatings Technology,2012,206(19-20),4021.
39 Liu K, Li Y J, Wang J, et al. Materials and Design,2015,87,66.
40 Wu W T, Zhang Y, Song B H. Journal of Shijiazhuang Tiedao University,2017,30(2),105(in Chinese).
吴文涛,张洋,宋博瀚.石家庄铁道大学学报(自然科学版),2017,30(2),105.
41 Cheng Y, Dong G, Chen G X, et al. Materials for Mechanical Enginee-ring,2014,38(9),24(in Chinese).
成阳,董刚,陈国喜,等.机械工程材料,2014,38(9),24.
42 Hu Y L, Lin X, Yu X B, et al. Journal of Alloys and Compounds,2017,711,267.
43 Ma Q S, Li Y J, Wang J. International Journal of Refractory Metals and Hard Materials,2017,64,225.
44 Yang L Q, Li Z Y, Zhang Y Q, et al. Applied Surface Science,2018,435,1187.
45 Xiang H, Xu Y, Zhang L, et al. Scripta Materialia,2006,55(4),339.
46 Yu T, Deng Q L, Dong G, et al. Applied Surface Science,2011,257,5098.
47 Zhao N, Tao L, Guo H, et al. Rare Metal Materials and Engineering,2017,46(8),2092.
48 Wang C L, Gao Y, Zeng Z C, et al. Journal of Alloys and Compounds,2017,727,278.