大气等离子喷涂Fe基涂层及其氩弧重熔层的组织与力学性能

doi:10.11896/cldb.201904022

Abstract
Figure/Table
References
Related Citation (15)

Download:
Export: BibTeX | EndNote (RIS)

Abstract In the present work, we applied tungsten inert gas arc (TIG) process to remelt a Fe-based coating which had been deposited by atmospheric plasma spraying technique, and characterized and determined the remelted coating’s microstructure and mechanical properties. The results showed that after TIG remelting, the lamellar structure, pores, unmelted particles and inclusions of the as-sprayed coating are eliminated, the porosity significantly decreases from 4% to 0.4% and the microstructure becomes quite compact. The as-sprayed coating consists mainly of microcrystalline region, nanocrystalline region and transition region, and has a low crystallinity and disordered atomic arrangement. The remelted coa-ting, on the contrary, contains single crystal region and (Fe,Cr)₂₃C₆phase, displays no microcrack at the pricipitates/matrix interfaces, and has better crystallization and atomic arrangement. A clear gap could be observed between the as-sprayed coating and the substrate, thus, the bon-ding formed between the as-sprayed coating and substrate is ascribed to mechanical bonding. However, the “white light belt” emerged at the interface between the remelted coating and substrate, the remelted coating was bonded with the substrate metallurgically. Compared with the as-sprayed coating, the average microhardness and elastic modulus of the remelted coating increased by 33.4% and 53.2% respectively, and the surface roughness of the remelted coating decreased by 43.2%. Therefore, TIG remelting process has considerable effect for improving the microstructure and mechanical properties of Fe-based coating.

Key words： TIG remelting Fe-based coating microstructure mechanical properties atmospheric plasma spraying

Published: 11 March 2019

CLC number:

TG174.44

Fund:This work was financially supported by the Natural Science Foundation of China (51675158, 51535011), the Natural Science Foundation of Hebei Province (E2016202325).

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	DONG Tianshun
	ZHENG Xiaodong
	LI Guolu
	WANG Haidou
	ZHOU Xiukai
	LI Yalong

Cite this article:

DONG Tianshun,ZHENG Xiaodong,LI Guolu, et al. Microstructure and Mechanical Properties of Atmospheric-plasma-sprayed
and TIG-remelted Fe-based Coating[J]. Materials Reports, 2019, 33(4): 678-683.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.201904022 OR http://www.mater-rep.com/EN/Y2019/V33/I4/678

Chen S Y, Ma G Z, Wang H D, et al. Tribology International,2016,101,25.2 Guo H J, Jia J H, Zhang Z Y, et al. Materials Review A: Review Papers,2013,27(2),38(in Chinese).国洪建,贾均红,张振宇,等.材料导报:综述篇,2013,27(2),38.3 Zhang X, Wang Z H, Lin J R, et al. Transactions of the China Welding Institution,2014,35(12),19(in Chinese).张欣,王泽华,林尽染,等.焊接学报,2014,35(12),19.4 Piao Z Y, Xu B S, Wang H D, et al. Tribology International,2010,43(1),252.5 Xu B S. Theory and technology of surface engineering, National Defense Industry Press, China,2010(in Chinese).徐滨士.表面工程的理论与技术,国防工业出版社,2010.6 Cui C, Ye F X, Song G R. Surface and Coatings Technology,2012,206(8),2388.7 Liu J, Bolot R, Costil S, et al. Surface & Coatings Technology,2016,292,132.8 Yi D L, Ye Y P, Yin B, et al. Tribology,2011,31(4),362.9 Serres N, Hlawka F, Costil S, et al. Wear,2011,270(10),640.10 Kang N, Verdy C, Coddet P, et al. Surface & Coatings Technology,2017,359,264.11 Wen Z H, Bai Y, Yang J F, et al. Surface & Coatings Technology,2015,281,62.12 Tian L H, Mao S H, Lu S, et al. Transactions of the China Welding Institution,2016,37(6),89(in Chinese).田立辉,毛淑滑,芦笙,等.焊接学报,2016,37(6),89.13 Yu B, He J, Liu Z D, et al. Vacuum & Cryogenics,2009,15(3),149(in Chinese).于斌,何俊,刘志栋,等.真空与低温,2009,15(3),149.14 Chen J B, Dong Y C, Wan L N, et al. Surface & Coatings Technology,2018,340,159.15 Zhang X C, Xu B S, Xuan F Z, et al. Surface & Coatings Technology,2011,205,3119.16 Yang X C, Li G L, Wang H D, et al.Surface Engineering,2016,1,1.17 Tian H L, Wei S C, Chen Y X, et al. Physics Procedia,2013,50,322.18 Zong X M, Li W, Wang J, et al. Surface Technology,2017,46(7),195(in Chinese).蹤雪梅,李稳,王井,等.表面技术,2017,46(7),195.19 Wang X H, Zou Z D, Song S L, et al. Wear,2006,260(7),705.20 Zhang K, Ma G, Jia Z H, et al. Materials Review,2012,26(S2),166(in Chinese).张科,马光,贾志华,等.材料导报,2012,26(S2),166.21 Yuan Z Z, Bao S L, Lu Y, et al. Journal of Alloys Compounds,2008,459,251.22 Zhi J Y, Shun Y T, Xia M Z, et al.Journal of the European Ceramic Society,2008,28,1143.