Abstract This study explored the protection of steel from chloride-induced corrosion by cement slurry coatings with calcined Mg-Al layered double hydroxides. The calcined Mg-Al hydrotalcite material was added to the cement slurry to prepare a composite cement slurry coating on the steel bar surface. The corrosion inhibition performance of composite cement slurry coatings on chloride ion corrosion in concrete simulated pore solution was studied by the isothermal adsorption experiment, linear polarization test (LP) and electrochemical impedance spectroscopy (EIS). In addition, the phase change of the cement slurry before and after the adsorption experiment was observed by X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FT-IR). The results showed that the incorporation of LDO could significantly increase the saturated adsorption capacity of cement slurry, and with the increase of LDO content, the comprehensive effect of composite cement slurry coatings from chloride-induced was enhanced. LDO composite coatings controlled-release mechanism attributed to the recovery of lamellar mechanism could effectively adsorb chloride ions and release hydroxyl ions, which could effectively prevent the erosion of chloride ions.

Key words： calcined Mg-Al layered double hydroxides cement slurry coatings chloride ions adsorption corrosion inhibition performance

Published: 21 December 2018

CLC number:

TU52

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	MEI Youjing
	XU Jinxia
	JIANG Linhua
	CHEN Ping
	TAN Qiping

Cite this article:

MEI Youjing,XU Jinxia,JIANG Linhua, et al. Protecting of Steel from Chloride-induced Corrosion by Cement Slurry Coatings with Calcined Mg-Al Layered Double Hydroxides[J]. Materials Reports, 2018, 32(22): 3941-3947.

URL:

http://www.mater-rep.com/EN/10.11896/j.issn.1005-023X.2018.22.018 OR http://www.mater-rep.com/EN/Y2018/V32/I22/3941

1 Zheng L, Yang H. Influence of organic inhibitors on the corrosion behavior of steel rebar inside mortar specimens immersed in saturated NaCl solution[J]. Acta Physico-Chimica Sinica,2010(9):2354(in Chinese).
郑雷刚,杨怀玉.饱和NaCl溶液浸泡下混凝土试块中有机阻锈剂对钢筋腐蚀行为的影响[J].物理化学学报,2010(9):2354.
2 汪红.浅谈钢筋保护层的重要性及控制[J].中国新技术新产品,2016(16):110.
3 Mahmoud M R, Soliman M A, Rashad G M. Performance appraisal of foam separation technology for removalof Co(Ⅱ)-EDTA com-plexes intercalated into in-situ formed Mg-Al layered double hydro-xide from radioactive liquid waste[J]. Chemical Engineering Journal,2017,326:781.
4 Lv L,He J, Wei M, et al. Uptake of chloride ion from aqueous solution by calcined layered double hydroxides: Equilibrium and kinetic studies[J]. Water Research.2006,40:735.
5 Hu Y C, Ren Y H, Rong M X, et al. Study on removal performance of chlorine anion by calcined hydrotalcite[J]. Chemical Engineer,2005(2):7(in Chinese).
胡玉才,任玉华,荣明霞,等.焙烧水滑石对氯离子的去除性能研究[J].化学工程师,2005(2):7.
6 Tang L, Nilsson L O. Chloride binding capacity and binding isotherms of OPC pastes and mortars[J]. Cement and Concrete Research,1993,23(2):247.
7 Xu J, Song Y, Tan Q, et al. Chloride absorption by nitrate, nitrite and aminobenzoate intercalated layered double hydroxides[J]. CrossMark,2017,52(10):5908.
8 Hwang I, Batchelor B. Reductive dechlorination of chlorinated methanes in cement slurries containing Fe(Ⅱ)[J]. Chemosphere,2002,48(2):1019.
9 Rivera-Corral J O, Fajardo G, Arliguie G, et al. Corrosion behavior of steel reinforcement bars embedded in concrete exposed to chlorides: Effect of surface finish[J]. Construction and Building Mate-rials,2017,147:815.
10 Wu Y H, Luo S X, Fu Y Y, et al. EIS characteristics of the steel in concrete in environment containing chloride ion[J]. Surface Techno-logy,2011(3):65(in Chinese).
伍远辉,罗宿星,付盈盈,等.氯离子环境下混凝土钢筋的电化学阻抗谱特征[J].表面技术,2011(3):65.
11 Menezes Dos Santos R M, Lima Gonsalves R G, Leopoldo Constantino V R, et al. Adsorption of Acid Yellow 42 dye on calcined layered double hydroxide: Effect of time, concentration, pH and temperature[J]. Applied Clay Science,2017,140:132.
12 Shi J J, Sun W. Equivalent circuits fitting of electrochemical impe-dance spectroscopy for corrosion of reinforcing steel in concrete[J]. Corrosion Science and Protection Technology, 2011(5): 387(in Chinese).
施锦杰,孙伟.等效电路拟合钢筋锈蚀行为的电化学阻抗谱研究[J].腐蚀科学与防护技术,2011(5):387.
13 Geng G Q, Shi J J, Sun W. Comparison of electrochemical measurements for steel corrosion in simulated concrete pore solution[J]. Journal of Southeast University (Natural Science Edition), 2011(2): 382(in Chinese).
耿国庆,施锦杰,孙伟.混凝土模拟液中钢筋腐蚀电化学测试结果比较[J].东南大学学报(自然科学版),2011(2):382.
14 Sigircik G, Tuken T, Erbil M. Assessment of the inhibition efficiency of 3,4-diaminobenzonitrile against the corrosion of steel[J]. Corrosion Science,2016,102:437.
15 Jiang S, Jiang L, Wang Z, et al. Deoxyribonucleic acid as an inhi-bitor for chloride-induced corrosion of reinforcing steel in simulated concrete pore solutions[J]. Construction and Building Materials,2017,150:238.
16 Liang Y, Huang J, Lin X, et al. The effect of chloride on concrete under sulfate attack[J]. Journal of Fuzhou University,2011,39(6):947.