海洋环境下钢材表面镀铝工艺的研究进展

doi:10.11896/j.issn.1005-023X.2018.21.018

Abstract
Figure/Table
References
Related Citation (3)

Download:

Full Text ( PDF ) (2079KB)
Export: BibTeX | EndNote (RIS)

Abstract Steels have found extensive application in the field of marine engineering as one species of essential structural materials, and the continuous mounting support for marine resource utilization exaggerates the demand for steel products. The exposure of steel to harsh marine environment will easily lead to severe corrosion for the sake of the reaction between the steel and the surroun-ding chlorine- and sulfur-containing corrosive medium. Meanwhile, other minus circumstances, such as tides, sunlight, dissolved oxygen, microorganisms, abyssal sea pressure, and hydrothermal fluid-induced high temperature usually aggravate the corrosion of steels. These would seriously affect service safety, lifespan and reliability of marine engineering facilities.
Therefore, aiming at improving the corrosion resistance of steel, researchers and engineers have paid much interest to the surface treatment techniques exemplified by coating preparation. Aluminum and its alloys can form a dense oxide film on the surface in corrosive and high-temperature oxidation environment. Aluminum coatings prepared on steel surfaces through different processes have been proved to have long-term corrosion protection efficacy.
Currently, the common methods for preparing aluminum coatings include hot dipping, electroplating, embedding aluminizing, thermal spraying, etc. Owing to its simple operation and low cost, hot dip aluminizing process has been widely used in marine infrastructures, e.g. marine platforms, wharfs, bridges. Electroplating technique enjoys the advantage of controllable coating thickness, microstructure and morphology by moderate preparation conditions and adjustable process parameters, and has successfully achieved precise deposition of aluminum coatings on tiny parts. Furthermore, the newly emerging green and eco-friendly ionic liquid systems facilitate the improvement of electroplating efficiency and coating quality while reducing the pollution to environment. Aluminum coatings prepared by powder embedding process have excellent high-temperature oxidation resistance, which are widely used in marine oil and gas field. Moreover, low-temperature embedding aluminizing process can overcome the problem of high-temperature-induced mechanical properties deterioration with respect to traditional aluminizing process. In addition, the development of slurry aluminizing and vapor phase aluminizing has promoted the practical application of the embedding aluminizing process. Thermal spraying techniques, including flame spraying, arc spraying and cold spraying, are the most widely used aluminizing techniques which could obtain high-anti-corrosion protective surface against marine environment.
This review provides a vivid description of the research progress with respect to aluminizing process used to prepare aluminum coatings on surface of steels which serve under the marine environment, including hot dipping, electroplating, embedding aluminizing and thermal spraying. It also gives a brief prospective discussion over the potential application and development tendency of these various aluminizing techniques.

Key words： marine environment steel surface aluminizing process hot dipping electroplating embedding aluminizing thermal spraying

Published: 21 November 2018

CLC number:

TB37

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	WANG Yao
	ZHAO Xueni
	DANG Xin'an
	WANG Xudong
	ZHANG Li
	YANG Jianjun
	HE Fuzhen
	ZHANG Weigang
	LIU Qingyao

Cite this article:

WANG Yao,ZHAO Xueni,DANG Xin'an, et al. Aluminizing Steel Surface for Providing Protection in Marine Environment: a Technological Review[J]. Materials Reports, 2018, 32(21): 3805-3813.

URL:

http://www.mater-rep.com/EN/10.11896/j.issn.1005-023X.2018.21.018 OR http://www.mater-rep.com/EN/Y2018/V32/I21/3805

1 周廉,等.中国海洋工程材料发展战略咨询报告[M].北京:化学工业出版社,2014.
2 Jeffrey R, Melchers R E.Corrosion of vertical mild steel strips in seawater[J].Corrosion Science,2009,51(10):2291.
3 Liu H D,Wang D Z,Wang C G,et al.A review of corrosion fatigue cracks for stainless steels in marine environments[J].Corrosion Research,2017,31(4):60(in Chinese).
刘海定,王东哲,王春光,等.海水环境中不锈钢腐蚀疲劳裂纹研究进展[J].腐蚀研究,2017,31(4):60.
4 Ma Y T,Li Y,Wang F H.The atmospheric corrosion kinetics of low carbon steel in a tropical marine environment[J].Corrosion Science,2010,52(5):1796.
5 Shi Z M,Cao J B,Han F S.Preparation and characterization of Fe-Al intermetallic layer on the surface of T91 heat-resistant steel[J].Journal of Nuclear Materials,2014,447:77.
6 Sun J,Wan M P.Compartion of corrosion resisting properties of hot dip garvanizing and aluminium coating of steel parts and their application[J].Modern Machinery,2010(2):75(in Chinese).
孙捷,万明攀.热浸镀锌和热浸镀铝钢铁件的耐蚀性能比较及应用[J].现代机械,2010(2):75.
7 Lemmens B,Springer H,Graeve I D, et al.Effect of silicon on the microstructure and growth kinetics of intermetallic phases formed during hot-dip aluminizing of ferritic steel[J].Surface & Coatings Technology,2017,319:104.
8 Takata N, Nishimoto M, Kobayashi S, et al.Morphology and formation of Fe-Al intermetallic layers on iron hot-dipped in Al-Mg-Si alloy melt[J].Intermetallics,2014,54(12):136.
9 Cheng W J, Wang C J.Growth of intermetallic layer in the aluminide mild steel during hot-dipping[J].Surface & Coatings Technology,2009,204(6-7):824.
10 Awan G H, Hasan F U.The morphology of coating/substrate interface in hot-dip aluminized steels[J].Materials Science and Enginee-ring A,2008,472(1-2):157.
11 Wu J J, Li K, Fan Y Z. The formation process of transition layer of steel wire hot-dipped galfan by sendzimir process[J].Advanced Materials Research,2012,383-390:3917.
12 Wu Y K.Comparison of hot-dip aluminizing technology for iron and steel wares(Ⅰ)—One bath fluxing route[J].Materials Protection,2011,10(44):71(in Chinese).
吴元康. 钢铁件热浸镀铝工艺比较(Ⅰ)—一浴溶液法[J].材料保护,2011,10(44):71.
13 Jeshvaghani R A, Emami M, Shafiee O, et al.Study on formation and characterization of iron aluminide coatings on 9Cr-1Mo steel substrate[J].Surface & Coatings Technology,2014,240(3):365.
14 Zhao G H, Zhao J H.Surface modification of die casting mold steel by a composite technique of hot-dipping and plasma electrolytic oxidation[J].Rare Metals,2012,31(4):362.
15 Yu S R, Xu S M, Xing H R.Hot dip aluminizing process and surface morphology on stainless steel surface[J].Hot Working Technology,2015,44(10):153(in Chinese).
于思荣,徐淑苗,邢海瑞.不锈钢表面热浸镀铝工艺及表面形貌[J].热加工工艺,2015,44(10):153.
16 Kang S, Han K, Kim K, et al.Formation behavior of an intermetallic compound layer during the hot dip aluminizing of cast iron[J].ISIJ International,2012,52(7):1342.
17 Zhang W, Liu A P, Jin W Z.Diffusion behavior of aluminum atoms in hot dip RE-aluminizing[J].Advanced Materials Research,2011,328-330:1523.
18 Wen J B, Zhang W, Li X Y, et al. The influence of La on the corrosion resistance of hot-dip aluminized steel[J].Materials Science Forum,2005,475-479:3851.
19 Wen J B, Li Q A, Zhao W X, et al.Investigation of properties of hot-dipped Ce-rich rare earth aluminum alloy upon condition of corrosion environment[J].Acta Scientiarum Naturalium Universitatis Sunyat-seni,2003,42(sup.):41.
20 Sun W, Cai Q Z, Luo Q.Effects of rare earth on microstructure and corrosion resistance of hot-dip aluminum coating[J].China Surface Engineering,2010,23(6):24(in Chinese).
孙伟,蔡启舟,罗强.RE对热浸镀铝镀层组织及耐蚀性能的影响[J].中国表面工程,2010,23(6):24.
21 Cheng W J, Wang C J.High-temperature oxidation behavior of hot-dipped aluminide mild steel with various silicon contents[J].Applied Surface Science,2013,274(6):258.
22 Takata N, Nishimoto M, Kobayashi S, et al.Crystallography of Fe₂Al₅ phase at the interface between solid Fe and liquid Al[J].Intermetallics,2015,67:1.
23 Wulf S E, Holstein N, Krauss W.Influence of deposition conditions on the microstructure of Al-based coatings for applications as corrosion and anti-permeation barrier[J].Fusion Engineering & Design,2013,88(9-10):253.
24 Wang J H, Zhang A P.Preparation and properties of aluminum coa-ting electrodeposited from AlCl₃+LiAlH₄ organic solvent[J].Electroplating and Finishing,2007,26(2):9(in Chinese).
王吉会,张爱平.AlCl₃+LiAlH₄有机溶剂中铝镀层的制备与性能研究[J].电镀与精饰,2007,26(2):9.
25 Liu Q X, Abedin S Z E, Endres F. Electroplating of mild steel by aluminium in a first generation ionic liquid: A green alternative to commercial Al-plating in organic solvents[J].Surface & Coatings Technology,2006,201(3-4):1352.
26 Abedin S Z E, Endres F. Challenges in the electrochemical coating of high-strength steel screws by aluminum in an acidic ionic liquid composed of 1-Ethyl-3-methylimidazolium chloride and AlCl₃[J].Journal of Solid State Electrochemistry,2013,17(4):1127.
27 Sangjae K, Salman S, Liang Y, et al.Aluminum electroplating in AlCl₃/dimethylsulfone electrolyte[C]∥The 19th Interfnish World Congress & Exhibition.Beijing,2016.
28 Zhang S M, Zhou Y Q.Electroplating of aluminum from organic solutions[J].Corrosion and Protection,2000,21(2):57(in Chinese).
张守民,周永洽.有机溶液中铝的电镀[J].腐蚀与防护,2000,21(2):57.
29 Miyake M, Tajikara S, Hirato T, et al.Fabrication of TiAl₃ coating on TiAl-based alloy by Al electrodeposition from dimethylsulfone bath and subsequent annealing[J].Surface and Coatings Technology,2011,205(21):5141.
30 Miyake M, Motonami H, Shiomi S, et al.Electrodeposition of purified aluminum coatings from dimethylsulfone-AlCl₃ electrolytes with trimethylamine hydrochloride[J].Surface & Coatings Technology,2012,206(19-20):4225.
31 Jafarian M, Maleki A, Danaee I, et al.Electrodeposition of Al,Mn,and Al-Mn Alloy on aluminum electrodes from molten salt ( AlCl₃-NaCl-KCl )[J].Journal of Applied Electrochemistry,2009,39(8):1297.
32 Feng Q Y, Ding Z M, Zhao Z Y, et al.A new technology of composition treatment of steel heat treatment in molten salt and its surface aluminum-electroplating[J].Locomotive and Rolling Stock Technology,2003(6):5(in Chinese).
冯秋元,丁志敏,赵振燕,等.钢的盐浴热处理及表面电镀铝复合处理新工艺[J].机车车辆工艺,2003(6):5.
33 Nayak B, Misra M M.The electrodepesition of aluminium on mild steel from a molten alumiuium chloride-sodium chloride bath[J].Applied Electrochemistry,1979,9:699.
34 Zhou Q L, Shen T, Xue L H, et al.Electroplating aluminum on steel in inorganic molten salt[J].Special Casting and Nonferrous Alloys,2010,30(8):748(in Chinese).
周启来,沈涛,薛丽红,等.钢基材表面无机熔融盐电镀铝的研究[J].特种铸造及有色合金,2010,30(8):748.
35 Shu J J.Microstructure and corrosion resistance of aluminum coating electroplated on low carbon steel from low-temperature AlCl₃-NaCl-KCl inorganic molten salt[J].Materials Protection,2010,43(1):46(in Chinese).
舒均杰. 低温AlCl₃-NaCl-KCl三元无机熔盐体系电镀铝工艺[J].材料保护,2010,43(1):46.
36 Ding Z M, Feng Q Y, Song J M, et al.Effect of current density on morpho-logy of electrodeposition aluminum crystal from molten salts[J].Transactions of Materials and Heat Treament,2012,33(9):129(in Chinese).
丁志敏,冯秋元,宋建敏,等.电流密度对熔盐电镀铝晶粒形貌的影响[J].材料热处理学报,2012,33(9):129.
37 Ding Z M, Feng Q Y, Shen C B, et al.Rule of formation of aluminum electroplating layer on Q235 steel[J].Journal of Environmental Sciences,2011,23:S138.
38 Abbott A P, Frisch G, Ryder K S.Electroplating using ionic liquids[J].Annual Review of Materials Research,2013,43(1):335.
39 Takahashi H, Matsushima H, Ueda M.Al film electrodeposition from the AlCl₃-EMIC electrolyte under a magnetic field[J].Journal of the Electrochemical Society,2017,164(8):H5165.
40 Uehara K, Yamazaki K, Gunji T, et al.Evaluation of key factors for preparing high brightness surfaces of aluminum films electrodeposi-ted from AlCl₃-1-ethyl-3-methylimidazolium chloride-organic additive baths[J].Electrochimica Acta,2016,215:556.
41 Zhang G K, Chen C A, Luo D L, et al.An advance process of aluminum rich coating as tritium permeation barrier on 321 steel workpiece[J].Fusion Engineering & Design,2012,87(7-8):1370.
42 Jiang T, Brym M J C, Dubé G, et al. Electrodeposition of aluminium from ionic liquids:Part Ⅱ—Studies on the electrodeposition of aluminum from aluminum chloride (AlCl₃)-trimethylphenylammonium chloride (TMPAC) ionic liquids[J].Surface and Coatings Technology,2006,201(1-2):10.
43 Chang J K, Chen S Y, Tsai W T, et al.Improved corrosion resistance of magnesium of alloy with a surface aluminum coating electrodeposition in ionic liquid[J].Journal of electrochemical Society,2008,155(3):C112.
44 Bozza F, Bolelli G, Giolli C, et al.Diffusion mechanisms and microstructure development in pack aluminizing of Ni-based alloys[J].Surface & Coatings Technology,2014,239:147.
45 Sun Y H, Dong J, Zhao P Z, et al.Formation and phase transformation of aluminide coating prepared by low temperature aluminizing process[J].Surface & Coatings Technology,2017,330:234.
46 Zhan Z L, Liu Z, Liu J X, et al.Microstructure and high-temperature corrosion behaviors of aluminide coatings by low-temperature pack aluminizing process[J].Applied Surface Science,2010,256:3874.
47 Montero X, Demler I, Kuznetsov V, et al.Factors governing slurry aluminization of steels[J].Surface & Coatings Technology,2017,309:179.
48 Eslami A, Arabi H, Rastegari S.Gas phase aluminizing of a nickel base superalloy by a single step HTHA aluminizing process[J].Canadian Metallurgical Quarterly,2009,48(1):91.
49 Wu X, Weng D, Zhao S, et al.Influence of an aluminized intermediate layer on the adhesion of a γ-Al₂O₃ washcoat on FeCrAl[J].Surface & Coatings Technology,2005,190(2):434.
50 Zhou Z H, Xie F, Hu J.A novel powder aluminizing technology assisted by direct current field at low temperatures[J].Surface and Coa-tings Technology,2008,203:23.
51 Guo S, Wang Z B, Lu K.An aluminide surface layer containing lower-Al on ferritic-martensitic steel formed by lower-temperature aluminization[J].Journal of Materials Science & Technology,2015,31(12):1268.
52 Bates B L, Wang Y Q, Zhang Y, et al.Formation and oxidation performance of low-temperature pack aluminide coatings on ferritic-martensitic steels[J].Surface and Coatings Technology,2009,204(6-7):766.
53 Lin R Q, Fu C, Liu M, et al.Microstructure and oxidation behavior of Al+Cr co-deposited coatings on nickel-based superalloys[J].Surface and Coatings Technology,2017,310:273
54 Majumdar S, Paul B, Kain V, et al.Formation of Al₂O₃/Fe-Al layers on SS 316 surface by pack aluminizing and heat treatment[J].Mate-rials Chemistry and Physics,2017,190:31.
55 Ji W W, Song Y P, Chen K, et al.Effect of RE elements on the microstructure and properties of aluminizing layer of 40Cr steel[J].Chinese Rare Earths,2009,30(6):55(in Chinese).
纪文文,宋月鹏,陈克,等.稀土元素对40Cr钢渗铝层组织性能的影响研究[J].稀土,2009,30(6):55.
56 Zhu L M, Yang J H, Wang C S, et al.Microstructure and oxidation behavior of novel CeO₂-modified aluminizing coating[J].Transactions of Materials and Heat Treament,2007,28(2):110(in Chinese).
朱利敏,杨景红,王长生,等.CeO₂改性渗铝层及其氧化性能研究[J].材料热处理学报,2007,28(2):110.
57 Dutta R S, Majumdar S, Laik A, et al.Formation and characterization of aluminide coatings on alloy 800 substrate[J].Surface and Coatings Technology,2011,205:4720.
58 Xiang Z D, Datta P K.Relationship between pack chemistry and aluminide coating formation for low-temperature aluminisation of alloy steels[J].Acta Materialia,2006,54(17):4453.
59 Zhan Z L, He Y D, Wang D R, et al.Preparation of aluminide coatings at relatively low temperatures[J].Transactions of Nonferrous Metals Society of China,2006,16(2):647.
60 Huang M, Wang Y.Research progress of low-temperature pack aluminizing and its potential application on oil-casing steel and pipeline steel[J].Hot Working Technology,2012,41(8):127(in Chinese).
黄敏,王宇.低温包埋渗铝及其在石油管材防腐蚀应用中的研究进展[J].热加工工艺,2012,41(8):127.
61 Luyckx S, Machio C N.Characterization of WC-VC-Co thermal spray powders and coatings[J].International Journal of Refractory Metals and Hard Materials,2007,27(1):11.
62 Yan L D, Yi P, Xiao K, et al.The research of the pure zinc and Zn-Al alloy coating[J].Corrosion and Protection,2015,36(S2):92(in Chinese).
颜利丹,易盼,肖葵,等.纯锌及锌铝合金涂层的性能研究[J].腐蚀与防护,2015,36(S2):92.
63 Chang X, Han F H, Zhang X B, et al.Research on aluminum coating by flame spraying[J].Journal of Chongqing University of Technology (Natural Science),2012,26(6):42(in Chinese).
昌霞,韩付会,张小彬,等.火焰喷涂铝涂层[J].重庆理工大学学报(自然科学),2012,26(6):42.
64 Zhang X B, Chang X, Han F H, et al. Researches on aluminum coating by flame spraying on Q235 steel surface[J].Advanced Materials Research,2012,472-475:2775.
65 Diamantogiannis G, Apostolopoulos C A, Nikolakopoulos P G.Mechanical behavior of B500c steel with an aluminum layer coating in a marine environment[J].Journal of Materials in Civil Engineering,2015,27(4):04014155.
66 Rodriguez R M H P, Paredes R S C, Wido S H, et al. Comparison of aluminum coatings deposited by flame spray and by electric arc spray[J].Surface & Coatings Technology,2007,202(1):172.
67 Huang J, Liu Y, Yuan J, et al.Al/Al₂O₃ composite coating deposited by flame spraying for marine applications: Alumina skeleton enhances anti-corrosion and wear performances[J].Journal of Thermal Spray Technology,2014,23(4):676.
68 Esfahani E A, Salimijazi H, Golozar M A, et al.Study of corrosion behavior of arc sprayed aluminum coating on mild steel[J].Journal of Thermal Spray Technology,2012,1(6):1195.
69 Zhou J, Yang M, Wang R, et al.Annealing behavior of aluminum coating prepared by arc spraying on P355NL1 steel[J].Surface & Coatings Technology,2017,330:53.
70 Liu K, Ma P, Pu N, et al.Influence of silicon coating on the corrosion resistance of Zn-Al-Mg-RE-Si alloy[J].Journal of Rare Earths,2010,28:378.
71 Jiang Q, Miao Q, Liang W, et al.Corrosion behavior of arc sprayed Al-Zn-Si-RE coatings on mild steel in 3.5 wt% NaCl solution[J].Electrochimica Acta,2014,115:644
72 Li W Y, Jiang R R, Huang C J, et al.Effect of cold sprayed Al coating on mechanical property and corrosion behavior of friction stir welded AA2024-T351 joint[J].Materials & Design,2015,65:757.
73 Moridi A, Hassanigangaraj S M, Gualiano M, et al.Cold spray coa-ting:Review of material systems and future perspectives[J].Surface Engineering,2014,30(6):369.
74 Kim K S, Lee C H, Huh H, et al.Effect of stain rate on microstructure evolution and compressive deformation behavior of high-strength aluminum coating materials fabricated by the kinetic spray process[J].Materials Transactions,2015,56(4):605.
75 Li N, Li W Y, Yang X W, et al.Effect of powder size on the long-term corrosion performance of pure aluminium coatings on mild steel by cold spraying[J].Materials & Corrosion,2016,68(5):546.
76 Peter I, Aldwell B, Lupoi R, et al.The deposition of pure aluminium via cold spray for the corrosion protection of steel[C]∥International Thermal Spray Conference.Shanghai,2016.
77 Silva F S D, Bedoya J, Dosta S, et al. Corrosion characteristics of cold gas spray coatings of reinforced aluminum deposited onto carbon steel[J].Corrosion Science,2016,114:57.