微米级多孔聚苯乙烯-二乙烯苯微球的制备、改性及应用综述

doi:10.11896/j.issn.1005-023X.2018.17.019

Abstract
Figure/Table
References
Related Citation (1)

Download:

Full Text ( PDF ) (1496KB)
Export: BibTeX | EndNote (RIS)

Abstract  As a new type of functional material, microporous polymer microspheres have provoked worldwide research inte-rest. They have particle size ranging from 1 μm to 100 μm, and internal permanent pores from a few angstrom up to several thousands of angstrom in their drying state. Due to their characteristics such as good sphericity, large specific surface area, low density, strong adsorptivity, high mechanical strength and compatibility to various solvents with different polarity, microporous polymer particles have displayed extensive application potential in the fields of the biomedicine, analytical chemistry, environmental protection, catalyst supports and electronic products, etc. Among them, microporous poly(styrene-divinylbenzene) microspheres inherit the ge-neral characteristics of porous polymer microspheres, and moreover, acquire the advantages of favorable physical, chemical and thermal stability, lower production cost and wide industrial applications, as well as high surface reactivity. Thereby microporous poly(styrene-divinylbenzene) microspheres have become the most widely used porous polymer particles at present.
   Owing to their attractive market prospect, the preparation and functionalization of microporous poly(styrene-divinylbenzene) microspheres have become the research focuses and obtained great success. Over the past decades, various methodologies have been developed and applied to the manufacture of microporous poly(styrene-divinylbenzene) microspheres. Suspension polymerization is the traditional and simple method to prepare poly(styrene-divinylbenzene) microspheres but results in broad particle size distribution. Seed swelling method has advantages on preparing monodispersed poly(styrene-divinylbenzene) microspheres with large size and functional groups. Besides, we can also use precipitation polymerization to obtain monodispersed polymer microspheres, though poor crosslinking density and low yield as well as difficulty to gain porous and functionalized product make this method less promising. Preparing poly(styrene-divinylbenzene) microspheres with microengineering emulsification techniques, including membrane/microchannel emulsification and microfluidics, will alleviate to get controllable size distribution and favorable reproducibility of particle size/pore size distribution. Hence microengineering emulsification opens a new path for the preparation of porous polymer particles.
   On the other side, noticeable efforts have also been made to introduce different functional groups onto the surface of porous poly(styrene-divinylbenzene) microspheres to impart hydrophilicity, solubility and biological affinity, which enable more diversified use, e.g. chromatographic packing, catalyst supports, biomedical materials and adsorbents.
   This article pioneers the summary over preparation and functionalization methods, important factors influencing pore size and distribution, with respect to microporous poly(styrene-divinylbenzene) microspheres. It also sketches out the appliance situation in recent years, and makes prospective discussion on the future development.

Key words： microporous poly(styrene-divinylbenzene) microspheres suspension polymerization seed swelling precipitation polymerization microengineering emulsification functionalization modification

Published: 19 September 2018

CLC number:

TQ325.2

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	BAO Jianmin
	YAN Zhiying
	LI Youxin

Cite this article:

BAO Jianmin,YAN Zhiying,LI Youxin. Microporous Poly(Styrene-Divinylbenzene) Microspheres: Preparation, Modification and Application[J]. Materials Reports, 2018, 32(17): 3060-3067.

URL:

http://www.mater-rep.com/EN/10.11896/j.issn.1005-023X.2018.17.019 OR http://www.mater-rep.com/EN/Y2018/V32/I17/3060

1 Huck C W, Bonn G K. Poly(styrene-divinylbenzene) based media for liquid chromatography[J].Chemical Engineering & Technology,2005,28(12):1457.
2 Zatirakha A V, Smolenkov A D, Shpigun O A. Preparation and chromatographic performance of polymer-based anion exchangers for ion chromatography: A review[J].Analytica Chimica Acta,2016,904:33.
3 Qin X. Synthesis and application of monodisperse polystyrene microspheres based on liquid biochips[D].Xiamen: Xiamen University,2009(in Chinese).
秦学.基于构建液相芯片的聚苯乙烯微球的合成及应用[D].厦门:厦门大学,2009.
4 Han M, Gao X, Su J Z, et al. Quantum-dot-tagged microbeads for multiplexed optical coding of biomolecules[J].Nature Biotechnology,2001,19(7):631.
5 Wang Z. Synthesis and application of magnetic nanocomposite polymer microspheres[D].Suzhou: Soochow University,2016(in Chinese).
王珍.磁性纳米复合高分子微球的制备与应用[D].苏州:苏州大学,2016.
6 Liu Q Q, Wang L, Xiao A G. Research progress in macroporous styrene-divinylbenzene co-polymer microspheres[J].Designed Monomers & Polymers,2007,10(5):405.
7 Li S S, Zhang H J, Zhou M, et al. Progress on functionalization of polystyrene microsphere and its application[J].Modern Chemical Industry,2017,37(5):38(in Chinese).
李丝丝,张红静,周明,等.聚苯乙烯微球的功能化及其应用进展[J].现代化工,2017,37(5):38.
8 Gokmen M T, Prez F E D. Porous polymer particles-a comprehensive guide to synthesis, characterization, functionalization and applications[J].Progress in Polymer Science,2012,37(3):365.
9 Arshady R. Suspension, emulsion, and dispersion polymerization: A methodological survey[J].Colloid & Polymer Science,1992,270(8):717.
10 Erbay E, Okay O. Pore memory of macroporous styrene-divinylbenzene copolymers[J].Journal of Applied Polymer Science,1998,71(7):1055.
11 Liu Q Q, Li Y L, Shen S H, et al. Preparation and characterization of crosslinked polymer beads with tunable pore morphology[J].Journal of Applied Polymer Science,2011,121(2):654.
12 Ogino K, Sato H, Tsuchiya K, et al. Synthesis of monodisperse macroreticular styrene-divinylbenzene gel particles by a single-step swelling and polymerization method[J].Journal of Chromatography A,1995,699(1-2):59.
13 Cao T Y, Dai B. Syntheses and applications of monodisperse polymer microspheres with large size[J].Polymer Bulletin,1995,25(3):174(in Chinese).
曹同玉,戴兵.单分散大粒径聚合物微球的合成及应用[J].高分子通报,1995,25(3):174.
14 Ugelstad J, Kaggerud K H, Hansen F K, et al. Absorption of low molecular weight compounds in aqueous dispersions of polymer-oligomer particles, 2. A two-step swelling process of polymer particles giving an enormous increase in absorption capacity[J].Die Makromolekulare Chemie,1979,180(3):737.
15 Tuncel A, Tuncel M, Salih B. Electron microscopic observation of uniform macroporous particles. I. Effect of seed latex type and diluent[J].Journal of Applied Polymer Science,1999,71(14):2271.
16 Okubo M, Shiozaki M, Tsujihiro M, et al. Preparation of micron-size monodisperse polymer particles by seeded polymerization utilizing the dynamic monomer swelling method[J].Colloid & Polymer Science,1991,269(3):222.
17 Okubo M, Nakagawa T. Preparation of micron-size monodisperse polymer particles having highly crosslinked structures and vinyl groups by seeded polymerization of divinylbenzene using the dynamic swelling method[J].Colloid & Polymer Science,1992,270(9):853.
18 Bao J M, Xu H, Li Y X. Preparation and application progress of methacrylate-based chromatographic packings[J].Modern Chemical Industry,2015,35(8):31(in Chinese).
包建民,许慧,李优鑫.甲基丙烯酸酯类色谱填料的制备及应用研究进展[J].现代化工,2015,35(8):31.
19 Qiao H M. Preparation methods and characterization of porous polymer microspheres[J].Chinese Journal of Pharmaceuticals,2015,46(11):1245(in Chinese).
乔红梅.多孔聚合物微球的制备方法及表征[J].中国医药工业杂志,2015,46(11):1245.
20 Cheng C M, Micale F J, Vanderhoff J W, et al. Synthesis and cha-racterization of monodisperse porous polymer particles[J].Journal of Polymer Science Part A: Polymer Chemistry,1992,30(2):235.
21 Li K, Stöver H D H. Synthesis of monodisperse poly(divinylbenzene) microspheres[J].Journal of Polymer Science Part A: Polymer Chemistry,1993,31(13):3257.
22 Yang S, Sang E S, Choe S. Stable poly(methyl methacrylate-co-divinylbenzene) microspheres via precipitation polymerization[J].Journal of Polymer Science Part A: Polymer Chemistry,2005,43(6):1309.
23 Tan Z, Ma J, Chen H, et al. Synthesis of monodisperse crosslinked poly(styrene-co-divinylbenzene) microspheres by precipitation polymerization in acetic acid[J].Journal of Applied Polymer Science,2012,124(5):3799.
24 Hao D X, Gong F L, Wei W, et al. Porogen effects in synthesis of uniform micrometer-sized poly(divinylbenzene) microspheres with high surface areas[J].Journal of Colloid & Interface Science,2008,323(1):52.
25 Sugiura S, Nakajima M, Seki M. Preparation of monodispersed polymeric microspheres over 50 μm employing microchannel emulsification[J].Industrial & Engineering Chemistry Research,2002,41(16):4043.
26 Vladisavljevic＇ G T, Kobayashi I. Production of uniform droplets using membrane, microchannel and microfluidic emulsification devices[J].Microfluidics & Nanofluidics,2012,13(1):151.
27 Abbasian M, Ghaderi A, Namazi H, et al. Preparation of anion-exchange resin based on styrene-divinylbenzene copolymer obtained by suspension polymerization method[J].Polymer-Plastics Technology and Engineering,2011,50(15):1606.
28 Cetinkaya O, Duru M E, Ciçek H. Synthese and characterization of boronic acid functionalized macroporous uniform poly(4-chloromethylstyrene-co-divinylbenzene) particles and its use in the isolation of antioxidant compounds from plant extracts[J].Journal of Chromatography B Analytical Technologies in the Biomedical & Life Sciences,2012,909(1):51.
29 Gong B L, Li L, Zhu J X, et al. Synthesis of monodisperse poly(chloromethyl-styrene-co-divinylbenzene) beads and their application in separation of biopolymers[J].Journal of Separation Science,2005,28(18):2546.
30 Li J, Li H M. Functionalization of syndiotactic polystyrene with succinic anhydride in the presence of aluminum chloride[J].European Polymer Journal,2005,41(4):823.
31 Ye Z F, Meng Q Q, Lu S T. Adsorption of 2, 4, 6-trinitrotoluene on carboxylated porous polystyrene microspheres[J].Applied Surface Science,2012,258(8):3624.
32 Qu J B, Shao H H, Li J, et al. Hydrophilization of gigaporous polystyrene microspheres with saccharide as high-speed protein chromatography base support[J].Reactive & Functional Polymers,2012,72(9):606.
33 Qu J B, Xu Y L, Liu J Y, et al. Chemical coating polysaccharide on gigaporous polystyrene microspheres as a high-speed protein chromatography matrix[J].Polymer Engineering & Science,2016,56(12):1407.
34 Corradini C, Corradini D, Huber C G, et al. Synthesis of a polyme-ric-based stationary phase for carbohydrate separation by high-pH anion-exchange chromatography with pulsed amperometric detection[J].Journal of Chromatography A,1994,685(2):213.
35 Pirogov A V, Chernova M V, Nemtseva D S, et al. Sulfonated and sulfoacylated poly(styrene-divinylbenzene) copolymers as packing materials for cation chromatography[J].Analytical & Bioanalytical Chemistry,2003,376(5):745.
36 Hu Y G, Zhou Z P, Sheng W C. The sulfonation of porous poly(styrene-co-divinylbenzene) micro spheres and adsorption of bovine serum albumin[J].Ion Exchange and Adsorption,2010,26(4):334(in Chinese).
胡友根,周志平,盛维琛.多孔苯乙烯-二乙烯基苯共聚物微球的磺化及其对牛血清蛋白的吸附[J].离子交换与吸附,2010,26(4):334.
37 Liu J W, Wang Y, Li W X, et al. Octadecylamine-modified poly(glycidylmethacrylate-divinylbenzene) stationary phase for HPLC determination of N-nitrosamines[J].Talanta,2016,160:298.
38 Subri N N S, Cormack P A G, Md Jamil S N A, et al. Synthesis of poly(acrylonitrile-co-divinylbenzene-co-vinylbenzyl chloride)-derived hypercrosslinked polymer microspheres and a preliminary evaluation of their potential for the solid-phase capture of pharmaceuticals[J].Journal of Applied Polymer Science,2017,DOI:10.1002/app.45677.
39 Wang P Y, Zu J H, Wei Y Z. Synthesis and characterization of po-rous 4VP-based adsorbent for Re adsorption as analogue to 99Tc[J].Nuclear Science and Techniques,2017,28(2):23.
40 Zhou C, Yan J, Cao Z. Post crosslinking of macroporous styrene-divinylbenzene copolymers via pendant vinyl groups: Effect of the starting copolymers on the pore structure of the postcrosslinked products[J].Journal of Applied Polymer Science,2001,83(8):1668.
41 Faber M C, Berg H J V D, Challa G, et al. Polymer-bound thiamine models. Ⅳ. A simple synthetic route to immobilize a thiazolium salt to macroreticular polystyrene resins via a dimethylene spacer[J].Reactive Polymers,1989,11(89):117.
42 Li S, Wang K, Song C L, et al. Study on the preparation and pro-perty of higher hydrophilic poly(styrene-divinylbenzene) porous microsphere[J].New Chemical Materials,2010,38(4):100(in Chinese).
李森,王宽,宋春莲,等.高亲水性聚(苯乙烯-二乙烯基苯)多孔微球的制备及亲水性研究[J].化工新型材料,2010,38(4):100.
43 Fournier C, Leonard M, Coqleonard I L, et al. Coating polystyrene particles by adsorption of hydrophobically modified dextran[J].Langmuir,1995,11(7):2344.
44 Xu Y, Liu X N, Zhou J, et al. Simultaneous determination of β-methy-β-nitrostyrolene and its related substances by PS-DVB chro-matographic column and the structural analysis of its photo-isomerization product[J].Analytical Methods,2014,6(20):8284.
45 天津大学.环糊精-苯乙烯-二乙烯苯微球的制备及在手性分离中的应用:中国,106905486 A[P].2017-06-30.
46 Wang M H, Liu J W, Huang Z P, et al. Preparation of an agglome-rated ion chromatographic stationary phase with 2,3-ionene and its application in SO₄^2- analysis[J].Chinese Journal of Chromatography,2015,33(7):678(in Chinese).
王慕华,刘军伟,黄忠平,等.2,3-聚季铵盐附聚型离子色谱固定相的制备及其在SO₄^2-分析中的应用[J].色谱,2015,33(7):678.
47 Drake R, Sherrington D C, Thomson S J. High surface area polystyrene resin-supported Pt alkene hydrosilylation catalysts: Ultimate performance and ‘sting in the tail’[J].Reactive & Functional Polymers,2004,60:65.
48 Aguiar V M D, Souza A L F D, Galdino F S, et al. Sulfonated poly(divinylbenzene) and poly(styrene-divinylbenzene) as catalysts for esterification of fatty acids[J].Renewable Energy,2017,114:725.
49 Ince A, Bayramoglu G, Karagoz B, et al. A method for fabrication of polyaniline coated polymer microspheres and its application for cellulase immobilization[J].Chemical Engineering Journal,2012,189-190(2):404.
50 Zhang J N, Ding K, Han T, et al. Preparation and application of multi-target immunoaffinity columns with polystyrene-divinylbenzene (PS-DVB) as carrier[J].Food Science,2016,37(20):172(in Chinese).
张家宁,丁轲,韩涛,等.以聚苯乙烯-二乙烯苯为载体的多目标免疫亲和柱的制备及应用[J].食品科学,2016,37(20):172.
51 Fathy M, Moghny T A, Awadallah A E, et al. Study the adsorption of sulfates by high cross-linked polystyrene divinylbenzene anion-exchange resin[J].Applied Water Science,2017,7(1):309.
52 Hartmann J, Beyer R, Harm S. Effective removal of estrogens from drinking water and wastewater by adsorption technology[J].Environmental Processes,2014,1(1):87.
53 Kumar R, Jain S K, Misra R K, et al. Aqueous heavy metals remo-val by adsorption on β-diketone-functionalized styrene-divinylbenzene copolymeric resin[J].International Journal of Environmental Science & Technology,2012,9(1):79.