Abstract The microstructure and properties of Al-Mg-Si alloy conducting wire prepared by multi-pass ECAE process were studied by means of S4800 scanning electron microscope (SEM), Philips DM420 transmission electron microscope (TEM), SANS CMT5105 electronic universal material testing machine and QJ48 double arm DC bridge. The results show that the grain of Al-Mg-Si alloy conducting wire with an average size of 10 μm or even smaller can be prepared by 4 passes ECAE dynamic forming. The tensile strength of the conducting wire increases with the increase of Mg, Si contents, however, the elongation and equivalent decrease. After soaked at 160-170 ℃ for 7 h, tensile strength, elongation and equivalent conductivity of the Al-0.59%Mg-0.59%Si alloy conductor were about 305.71-309.63 MPa, 4.7%-5.4% and 55.18%IACS-56.33%IACS, respectively. Hence the electric conductivity properties of the Al-Mg-Si alloy conductor are greatly improved compared to traditional Al-Mg-Si alloy conductor (whose tensile strength and equivalent conductivity are 295 MPa and 52.5%IACS, respectively).

Key words： Al-Mg-Si alloy conductor multi-pass ECAE dynamic forming aging treatment microstructure mechanical property electrical conductivity

Published: 02 May 2018

CLC number:

TG156

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	ZHOU Tianguo
	CHEN Tiantian
	SU Xin
	XU Rui
	WU Xiaoyu
	HU Jing

Cite this article:

ZHOU Tianguo,CHEN Tiantian,SU Xin, et al. Microstructure and Properties of Al-Mg-Si Alloy Conductor Prepared by Multi-pass ECAE Dynamic Forming[J]. Materials Reports, 2017, 31(8): 17-20.

URL:

http://www.mater-rep.com/EN/10.11896/j.issn.1005-023X.2017.08.004 OR http://www.mater-rep.com/EN/Y2017/V31/I8/17

1 Zhou T G, Jiang Z Y, et al. Semi-solid continuous casting-extrusion of AA6201 redraw rods[J]. Mater Sci Eng A,2008,485:108.
2 Zhang Desheng, Liu Ping, Liu Xinkuan, et al. Research on progress of high-conductivity and high-strength of aluminum conductor material[J]. Mater Heat Treatment,2012,41(24):24(in Chinese).
章德胜, 刘平, 刘新宽, 等. 高导电率、高强度耐热铝合金导线材料的研究进展[J]. 材料热处理技术,2012,41(24):24.
3 Yuan Shengping, Pu Xiong, Zhang Guojun, et al. Effects of multiple precipitates on electrical conductivity of aged Al-Mg-Si alloys[J]. Chin Nonferrous Metals,2010,20(11):2070(in Chinese).
袁生平, 蒲雄, 张国君, 等. 多重时效析出第二相对Al-Mg-Si合金电导率的影响[J]. 中国有色金属学报,2010,20(11):2070.
4 Cai M, Field D P, Lorimer G W. A systematic comparison of static and dynamic aging of two Al-Mg-Si alloys[J]. Mater Sci Eng A,2004,373:65.
5 Zhou Tianguo,et al. Microstructures and properties of Al-Zr-B alloy wires prepared by continuous dynamic aging ECAE forming[J]. Shenyang University: Nat Sci,2016,28(3):173(in Chinese).
周天国, 等. 连续ECAE动态时效成形制备Al-Zr-B合金的组织与性能[J]. 沈阳大学学报:自然科学版,2016,28(3):173.
6 Joon-Yeon C, Aidang S. Microstructure and mechanical properties of Al-Mg-Si alloys after equal channel angular pressing at room temperature[J]. Mater Sci Eng A,2003,347(1-2):165.7 Emanuela C, Paola L. Influence of severe plastic deformation on agi-ng of Al-Mg-Si alloys[J]. Mater Sci Eng A,2005,410-411:226.
8 Kwon Y N, Lee Y S, Lee J H. Deformation behavior of Al-Mg-Si alloy at the elevated temperature[J]. J Mater Processing Technol,2007,187-188:533.
9 Tsao C S, Chen C Y, Jeng U S, et al. Precipitation kinetics and transformation of metastable phases in Al-Mg-Si alloys[J]. Acta Mater,2006,54:4621.
10 Gaber A, Afify N, Mostafa M S, et al. Effect of heat treatment on the precipitation in Al-1at%Mg-xat%Si(x=0.6, 1.0 and 1.6) alloys[J]. J Alloys Compd,2009,477(1-2):295.
11 Zhou Tianguo, Shi Lu, Cao Furong, et al. Effects of aging treatment on the properties of 6201 alloy wires formed by SCR technology[J]. Trans Mater Heat Treatment,2005,26(1):24(in Chinese).
周天国, 石路, 曹富荣, 等. 热处理对SCR成形6201铝合金性能的影响[J]. 材料热处理学报,2005,26(1):24.