Fe-Cr-Mo-W-V系热作模具钢高温热稳定性机理研究

doi:10.11896/j.issn.1005-023X.2018.06.014

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (2287KB)
Export: BibTeX | EndNote (RIS)

Abstract Three kinds of Fe-Cr-Mo-W-V hot working die steels (DM, H21 and H13) were prepared to investigate the thermal stability at 580—650 ℃. Utilizing the hardness measurement and scanning electron microscopy (SEM), an attempt was made to study the thermal stability of three hot working die steels. The results indicated that DM steel had a higher thermal stability than H21 and H13 steels during tempering. Besides, combined with transmission electron microscopy (TEM), the dilatometric data (conti-nuous heating transformation curves) during tempering were analyzed to determine the significance carbides resulting in high thermal stability in Fe-Cr-Mo-W-V steels. To improve the understanding of the thermal stability mechanism, the activation energy of the transformation of MC carbides from M₂C carbides in DM, H21 and H13 steels were determined as 163.9—204.1 kJ/mol, which reflect the diffusion of the solute atoms in the transformation reaction of M₂C and MC carbides is controlled by volume diffusion and dislocation pipe diffusion, DM steel own the highest activation energy as 204.1 kJ/mol. Furthermore, comparing the differences of the value electron structures in three steels, DM steel with excellent thermal stability shows the best electron structure.

Key words： thermal stability hot working die steel continuous heating transformation curve electron structure

Published: 25 March 2018

CLC number:

TG113

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	SHI Yuanji
	WU Xiaochun
	MIN Na

Cite this article:

SHI Yuanji,WU Xiaochun,MIN Na. Thermal Stability Mechanism of Fe-Cr-Mo-W-V Hot Working Die Steel[J]. Materials Reports, 2018, 32(6): 930-936.

URL:

http://www.mater-rep.com/EN/10.11896/j.issn.1005-023X.2018.06.014 OR http://www.mater-rep.com/EN/Y2018/V32/I6/930

1 Cser L, Geiger M, Lange K, et al. Tool life and tool quality in bulk metal forming[J].Proceedings of the Institution of Mechanical Engineers,Part B:Journal of Engineering Manufacture,1993,207(4):223.
2 Kim D H, Lee H C, Kim B M, et al. Estimation of die service life against plastic deformation and wear during hot forging processes[J].Journal of Materials Processing Technology,2005,166(3):372.
3 Shi Y J, Li J W, Wu X C, et al. Experimental and numerical study on the wear failure of hot forging die of automobile flange[J].Tribo-logy,2016,36(2):215(in Chinese).
施渊吉,黎军顽,吴晓春,等.汽车法兰盘热锻模具磨损失效的实验分析和数值研究[J].摩擦学学报,2016,36(2):215.
4 Abel A, Ham R K. The cyclic strain behaviour of crystals of aluminum-4 wt.% copper-ii. Low cycle fatigue[J].Acta Metallurgica,1966,14(11):1495.
5 McGrath J T, Bratina W J. Interaction of dislocations and precipitates in quench-aged iron-carbon alloys subjected to cyclic stressing[J].Acta Metallurgica,1967,15(2):329.
6 Thielen P N, Fine M E, Fournelle R A. Cyclic stress strain relations and strain-controlled fatigue of 4140 steel[J].Acta Metallurgica,1976,24(1):1.
7 Wan C M, Chou K C, Jahn M T, et al. Fatigue studies on dual-phase low carbon steel[J].Journal of Materials Science,1981,16(9):2521.
8 Krauss G. Tempering and structural change in ferrous martensitic structures[J].Phase Transformations in Ferrous Alloys,1983:101.
9 Yan W, Wang W, Shan Y, et al. Microstructural stability of 9-12%Cr ferrite/martensite heat-resistant steels[J].Frontiers of Materials Science,2013,7(1):1.
10 Medvedeva A, Bergström J, Gunnarsson S, et al. High-temperature properties and microstructural stability of hot-work tool steels[J].Materials Science and Engineering:A,2009,523(1):39.
11 Frisk K. Simulation of precipitation of secondary carbides in hot work tool steels[J].Materials Science and Technology,2012,28(3):288.
12 Davenport A T, Honeycomb R W K. The secondary hardening of tungsten steels[J].Metal Science,1975,9(1):201.
13 Kwon H, Lee K B, Lee J B, et al. Secondary hardening and fracture behavior in alloy steels containing Mo, W, and Cr[J].Metallurgical and Materials Transactions A,1997,28(13):775.
14 Mulholland M D, Seidman D N. Nanoscale co-precipitation and mechanical properties of a high-strength low-carbon steel[J].Acta Materialia,2011,59(5):1881.
15 Wen T, Hu X F, Song Y Y. Effect of tempering temperature on carbide and mechanical properties in a Fe-Cr-Ni-Mo high-strength steel[J].Acta Metallurgica Sinica,2014,50(4):447(in Chinese).
温涛,胡小锋,宋元元.回火温度对一种FeCrNiMo高强钢碳化物及其力学性能的影响[J].金属学报,2014,50(4):447.
16 Liu Q D, Liu W Q, Wang Z M, et al. 3D atom probe characterization of carbides precipitated in the Nb-V microalloyed steel[J].Acta Metallurgica Sinica,2008,7(3):786(in Chinese).
刘庆冬,刘文庆,王泽民,等.Nb-V微合金钢中碳化物析出的三维原子探针表征[J].金属学报,2008,7(3):786.
17 Onizawa T, Wakai T, Ando M, et al. Effect of V and Nb on precipitation behavior and mechanical properties of high Cr steel[J].Nuclear Engineering and Design,2008,238(2):408.
18 Speich G R, Leslie W C. Tempering of steel[J].Metallurgical Tran-sactions,1972,3(5):1043.
19 Samuel F H, Hussein A A. A comparative study of tempering in steel[J].Materials Science and Engineering,1983,58(1):113.
20 Wang L J, Cai Q W, Wu H B, et al. Effect of tempering temperature on the microstructure and mechanical properties of 1500 MPa grade steel directly quenched[J].Chinese Journal of Engineering,2010,32(9):1150(in Chinese).
王立军,蔡庆伍,武会宾,等.回火温度对1 500 MPa级直接淬火钢组织与性能的影响[J].北京科技大学学报,2010,32(9):1150.
21 Pacyna J, J drzejewska-Strach A, Strach M. The effect of manganese and silicon on the kinetics of phase transformations during tempering—Continuous heating transformation (CHT) curves[J]. Journal of Materials Processing Technology, 1997, 64(1-3): 311.
22 Zaj?c G, Pacyna J. The kinetics of phase transformations during tempering in structural steels with nickel[J].Journal of Materials Processing Technology,2005,162:442.
23 Jung M, Lee S J, Lee Y K. Microstructural and dilatational changes during tempering and tempering kinetics in martensitic medium-carbon steel[J].Metallurgical and Materials Transactions A,2009,40(3):551.
24 Nagakura S, Hirotsu Y, Kusunoki M, et al. Crystallographic study of the tempering of martensitic carbon steel by electron microscopy and diffraction[J].Metallurgical Transactions A,1983,14(6):1025.
25 Taylor K A, Chang L, Olson G B, et al. Spinodal decomposition during aging of Fe-Ni-C martensites[J].Metallurgical Transactions A,1989,20(12):2717.
26 Baker R G, Nutting J. The tempering of 2.25 Cr%-1% Mo steel after quenching and normalizing[J].J Iron Steel Inst,1959,202:257.
27 Inoue A, Masumoto T. Carbide reactions (M3C→M7C3→M23C6→M6C) during tempering of rapidly solidified high carbon Cr-W and Cr-Mo steels[J].Metallurgical Transactions A,1980,11(5):739.
28 Zhou Q,Wu X, Shi N, et al. Microstructure evolution and kinetic analysis of DM hot-work die steels during tempering[J].Materials Science & Engineering A,2011,528(18):5696.
29 Bhadeshia H, Honeycombe R. Steels: Microstructure and properties[M].Butterworth-Heinemann,2011:195.
30 Karagöz S, Fischmeister H F, Andrén H O, et al. Microstructural changes during overtempering of high-speed steels[J].Metallurgical Transactions A,1992,23(6):1631.
31 Kurzydłowski K J, Zieliński W. Mo2C→ M6C carbide transformation in low alloy Cr-Mo ferritic steels[J].Metal Science,1984,18(4):223.
32 Hu X B, Li L, Wu X C, et al. Coarsening behavior of M23C6 carbides after ageing or thermal fatigue in AISI H13 steel with niobium[J].International Journal of Fatigue,2006,28(3):175.
33 Dudova N, Kaibyshev R. On the precipitation sequence in a 10% Cr steel under tempering[J].ISIJ international,2011,51(5): 826.
34 Mittemeher E J, Cheng L, Van der Schaaf P J, et al. Analysis of nonisothermal transformation kinetics; tempering of iron-carbon and iron-nitrogen martensites[J].Metallurgical Transactions A,1988,19(4):925.
35 俞德刚. 铁基马氏体时效-回火转变理论及其强韧性[M].上海:上海交通大学出版社,2008:113.
36 Yu R H. Empirical electron theory of solids and molecules[J].Chinese Science Bulletin,1978,23(4):217(in Chinese).
余瑞璜. 固体与分子经验电子理论[J].科学通报,1978,23(4):217.
37 Zhang R L, Yu R H. An analysis of valence electron structure of Fe-C martensite[J].Acta Metallurgica Sinica,1984,20(4):279(in Chinese).
张瑞林,余瑞璜.Fe-C马氏体价电子结构分析[J].金属学报,1984,20(4):279.
38 刘志林. 合金价电子结构与成分设计[M]. 长春: 吉林科学技术出版社, 1989: 111.