REVIEW PAPER |
|
|
|
|
|
Advances in Persistence Phosphors Activated by Blue-light |
CHEN Bida1, GAN Guisheng1,2, WU Yiping1, OU Yanjie3
|
1 College of Materials Science and Engineering, Huazhong University of Science and Technology, Wuhan 430074; 2 College of Materials Science and Engineering,Chongqing University of Technology, Chongqing 400054; 3 Zhuoran Optoelectronics Co.Ltd, Jiangmen 529000 |
|
|
Abstract As it is energy savings, environmental friendliness and fast switching, white light-emitting diode (w-LED) has become the new generation of lighting sources. It is commonly used that applying blue LED chip to excite the yellow YAG∶Ce3+ phosphor to synthesis white light. However, adding the DC (direct current)/AC (alternating current) conversion and heat-dissipation radiators makes the w-LED too expensive, which restricts the further development of w-LED seriously. AC-LED, a LED device driven by city power, is the inevitable direction of LED development. Furthermore, it is possible that applying afterglow phosphors in AC-LED. This paper provides a review of the persistence phosphors motivated by blue light in AC-LED, and the length of afterglow time is calculated. What’s more, the afterglow intensity and the decay rates are analyzed at the same time. The results of the paper showed that the afterglow decay time of phosphors is Tx(6.67 ms≤Tx≤10 ms), and the minimum value of afterglow intensity is greater than 0.032 mcd/m2. Meanwhile, the decay rate of afterglow satisfied the forum (1) in the text, and the afterglow is occurred at T/2—2T/3,which is the most beneficial to eliminate flicker effect.
|
Published: 08 May 2018
|
|
|
|
1 Yuan X F, Shi X B, Shen M R, et al. Luminescent properties of Pr3+ doped (Ca,Zn)TiO3:Powders and films[J]. J Alloys Compd, 2009,485(1-2):83. 2 Allen M. Preferred embodiment to LED light string: US, 20030015968[P]. 2004-12-14 3 颜重光. 发展迅速的AC直接驱动LED光源技术[J]. 电子产品世界, 2009(2):64(in Chinese). Yan Chongguang. The rapid development of the AC LED light source technology[J]. Electron Product World, 2009(2):64. 4 满瑞,李秋俊.AC-LED 的研究现状与发展[J]. 电源技术,2011,36(7):1068(in Chinese). Man R,Li Q J.Current research and development of AC LED[J].Chin J Power Sources, 2011,36(7):1068. 5 Choi B H, Park I K, Kim D H. Ac light emitting device, driving device thereof, and driving method thereby:WO 2010058923[P].2010-03-11. 6 Wilkins A, Veitch J, Lehman B. LED lighting flicker and potential health concerns[C]∥Energy Conversion Congress & Exposition. Atlanta, 2010. 7 Gao Yuan, Li Lisong, Philip K T Mok. An AC powered converter-free LED driver with low flicker[C]∥ Asia & South Pacific Design Automation Conference. Macao, 2016. 8 Ma H, Lai J, Zheng C, et al. A high-efficiency quasi-single-stage bridgeless electrolytic capacitor-free high-power AC-DC driver for supplying multiple LED strings in parallel[J]. IEEE Trans Power Electron, 2016,31(8):5825. 9 Chen L, Zhang Y S, Xue C, et al. The green phosphor SrAl2O4∶Eu2+, R3+ (R=Y, Dy) and its application in alternating current light-emitting diodes[J]. Funct Mater Lett, 2013, 6:1350047. 10Chiao-Wen Yeh,Ye Li,Jing Wang, et al. Appropriate green phosphor of SrSi2O2N2∶Eu2+,Mn2+ for AC LEDs[J]. Optics Express, 2012, 20(16):18031. 11Chen L, Zhang Y, Liu F Y, et al. A new green phosphor of SrAl2O4∶Eu2+, Ce3+,Li+for alternating current driven light-emitting diodes[J].Mater Res Bull, 2012,47:4071. 12Blasse G. New luminescent materials[J].Chem Mater, 1989, 1(3):294. 13Tuomas Aitasalo, Jorma H?ls, H?gne Jungner, et al. Thermoluminescence study of persistent luminescence materials:Eu2+ and R3+-doped calcium aluminates, CaAl2O4∶Eu2+,R3+[J]. J Phys Chem B,2006,110(10):4589. 14Brito H F, H?ls J, Laamanen T, et al. Persistent luminescence machanisms:Human imagination at work[J].Opt Mater Express,2012,2(4):371. 15丁清秀,刘洪楷.无机发光材料[M].北京:化学工业出版社,1980:1. 16Wu Xiao. First-principles study on strontium aluminate long afterglow luminescent materials [D].Shenyang: Shenyang University of Technology, 2016(in Chinese). 吴霄.铝酸锶长余辉发光材料的第一性原理研究[D].沈阳:沈阳工业大学,2016. 17Xu Jiao. Preperation and photoluminescence properties of long-persistent phosphorescence doped with lanthanides [D].Lanzhou:Lanzhou University, 2015(in Chinese). 徐娇. 稀土长余辉材料的制备及发光性能研究[D].兰州:兰州大学,2015. 18Zeng Wei. Synthesis and luminescent properties of oxide yellow long persistent phosphors [D].Lanzhou:Lanzhou University,2016(in Chinese). 曾巍. 氧化物黄色长余辉材料的合成及发光性能研究[D]. 兰州:兰州大学,2016. 19Eeckhout K V D, Smet P F, Poelman D. Persistent luminescence in Eu2+-doped compounds:A review[J].Materials,2010,3(4):2536. 20Blasse G,Wanmaker W L,Wter Vrugt J, et al. Fluorescence of Eu2+activated silicates[J]. Philips Res Rep, 1968, 23:189. 21Barry T L. Equilibria and Eu2+Luminescenceof subsolidus phases bounded by Ba3MgSi2O8,Sr3MgSi2O8,and Ca3MgSi2O8[J]. J Electrochem Soc, 1968, 115(7):733. 22Jia D D, Wang X J, Yen W M. Delocalization, thermal ionization and energy transfer in singly doped and codoped CaAl4O7 and Y2O3[J].Phys Rev B,2004, 69:235113. 23Dorenbos P. Mechanism of persistent luminescence in Eu2+ and Dy3+ codoped aluminate and silicate compounds[J]. J Electrochem Soc, 2005, 152, H107. 24Bos A J J, Duijvenvoorde R M V, Kolk E V D, et al. Thermoluminescence excitation spectroscopy: A versatile technique to study persistent luminescence phosphors[J]. J Lumin, 2011, 131(7):1465. 25Bo Wang, Lin Hang, Yu Yunlong, et al.Ce3+/Pr3+∶YAGG:A long persistent phosphor activated by blue-light[J].J Am Ceram Soc,2014, 97(8):2539. 26Mu Zhongfei, Wang Yinhai, Hu Yihua, et al. The afterglow and thermoluminescence properties ofY3Al5O12∶Ce3+[J]. Acta Phys Sin, 2011,60(1):182(in Chinese) 牟中飞,王银海,胡义华,等. Y3Al5O12∶Ce3+的余辉和热释光特性[J]. 物理学报, 2011, 60(1):182. 27Jumpei Ueda, Keisuke Kuroishi, Setsuhisa Tanabe. Bright persistent ceramic phosphors of Ce3+-Cr3+-codoped garnet able to store by blue light[J]. Appl Phys Lett, 2014, 104(10):101904. 28Jumpei Ueda, Kotaro Aishima, Nishiura S, et al.Afterglow luminescence in Ce3+-doped Y3Sc2Ga3O12 ceramics[J].Appl Phys Express, 2011, 4(4):257. 29Xu Jian, Ueda Jumpei, Kuroishi K, et al. Fabrication of Ce3+-Cr3+ co-doped yttrium aluminium gallium garnet transparent ceramic phosphors with super long persistent luminescence[J]. Scr Mater,2015,102:47. 30Chen Hui, Lin Hang, Xu Ju,et al. Chromaticity-tunable phosphor-in-glass for long-lifetime high-power warm W-LEDs[J]. J Mater Chem C, 2015, 3(31):8080. 31Lin Zebin, Lin Hang, Xu Ju, et al. A chromaticity-tunable garnet-based phosphor-in-glass colorconverter applicable in w-LED[J].J Eur Ceram Soc, 2016,36(7):1723. 32Lin Hang, Wang Bo, Xu Ju, et al. Phosphor-in-glass for high-po-wered remote-type white AC-LED[J]. ACS Appl Mater Interfaces,2014, 6(23):21264. 33Jumpei Ueda, Keisuke Kuroishi, Setsuhisa Tanabe. Yellow persistent luminescence in Ce3+-Cr3+-codoped gadolinium aluminum gal-lium garnet transparent ceramics after blue-light excitation[J].Appl Phys Express, 2014, 7(6):297. 34Li Y Q, van Steen J E J, van Krevel J W H, et al. Luminescence properties of red-emitting M2Si5N8∶Eu2+ (M=Ca, Sr, Ba) LED conversion phosphors[J]. J Alloys Compd, 2006, 417(1-2):273. 35Xie R J, Hirosaki N, Suehiro T, et al. A simple, efficient synthetic route to Sr2Si5N8∶Eu2+-based red phosphors for white light-emitting diodes[J]. Cheminform, 2006, 38(4):5578. 36Wang Bo, Lin Hang, Xu Ju, et al. Design,preparation,and characterization of a novel red long-persistent perovskite phosphor:Ca3Ti2O7∶Pr3+[J].Inorg Chem, 2015, 54(23):11299. 37中国科学院福建物质结构研究所.一种AC-LED用镨掺杂钙钛矿型红色余辉发光材料及其制备方法:CN, 105295911[P].2016-02-03. 38Lin Hang, Xu Ju, Huang Qingming, et al. Bandgap tailoring via si doping in inverse-garnet Mg3Y2Ge3O12∶Ce3+ persistent phosphor potentially applicable in AC-LED[J]. ACS Appl Mater Interfaces,2015,7:21835. 39四川新力光源股份有限公司,中国科学院长春应用化学研究所.一种交流 LED发光装置:CN, 102468413[P].2014-10-29. 40天津理工大学.蓝光激发的橙红光磷光体及制备方法与余辉二极管:CN, 101186819[P].2008-05-28. 41江门市远大发光材料有限公司.一种具有余辉特性的高显色白光LED器件:CN, 102629655[P].2012-08-08. 42中山大学.一种黄色长余辉发光材料及其制备方法:CN, 103131415[P].2015-01-28. 43中国科学院福建物质结构研究所.一种用于AC-LED的黄色余辉微晶玻璃及其制备技术:CN, 104529165[P].2015-04-22. 44Lin Hang, Wang Bo, Huang Qingming, et al. Lu2CaMg2 (Si1-x-Gex)3O12∶Ce3+solid-solution phosphors: Bandgap engineering for blue-light activated afterglow applicable to AC-LED[J]. J Mater Chem C, 2016, 4:10329. 45Liang Yanjie. Design, preparation and properties of yttrium vanadate upconversion luminescent nanomaterials and germinate-based persistent phosphors[D].Jinan: Shandong University,2016(in Chinese). 梁延杰.钒酸钇上转换发光纳米材料和锗酸盐基长余辉发光材料的设计、制备与性能[D].济南:山东大学,2016. 46Rea M S. The IESNA lighting handbook: Reference&application[M]. New York: Illuminating Engineering society of North America, 2000: 44. 47Sakai R, Katsumata T, Komuro S,et al. Effect of composition on the phosphorescence from BaAl2O4∶Eu2+,Dy3+ crystals[J]. J Lumin, 1999, 85(1):149. 48Yuan Z X,Chang C K,Mao D L, et al. Effect of composition on the luminescent properties of Sr4Al14O25∶Eu2+,Dy3+phosphors[J]. J Alloys Compd, 2004, 377(1-2):268. |
|
|
|